WO1998033945A1 - Ferromagnetic amorphous metallic alloy and annealing method - Google Patents
Ferromagnetic amorphous metallic alloy and annealing method Download PDFInfo
- Publication number
- WO1998033945A1 WO1998033945A1 PCT/US1998/001898 US9801898W WO9833945A1 WO 1998033945 A1 WO1998033945 A1 WO 1998033945A1 US 9801898 W US9801898 W US 9801898W WO 9833945 A1 WO9833945 A1 WO 9833945A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- core
- annealed
- temperature
- annealing
- exciting power
- Prior art date
Abstract
Description
Claims