WO1999010421A1 - Rheology modification of interpolymers of alpha-olefins and vinyl aromatic monomers - Google Patents
Rheology modification of interpolymers of alpha-olefins and vinyl aromatic monomersInfo
- Publication number
- WO1999010421A1 WO1999010421A1 PCT/US1998/016213 US9816213W WO9910421A1 WO 1999010421 A1 WO1999010421 A1 WO 1999010421A1 US 9816213 W US9816213 W US 9816213W WO 9910421 A1 WO9910421 A1 WO 9910421A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sulfonyl azide
- polymer
- poly
- sulfonyl
- azide
- Prior art date
Abstract
Description
Claims