WO1999055740A1 - Production of ziegler-natta catalysts - Google Patents
Production of ziegler-natta catalysts Download PDFInfo
- Publication number
- WO1999055740A1 WO1999055740A1 PCT/EP1999/002719 EP9902719W WO9955740A1 WO 1999055740 A1 WO1999055740 A1 WO 1999055740A1 EP 9902719 W EP9902719 W EP 9902719W WO 9955740 A1 WO9955740 A1 WO 9955740A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- magnesium
- halide
- compound
- magnesium chloride
- titanated
- Prior art date
Abstract
Description
Claims