WO2000000651A9 - Alloy for battery grids - Google Patents
Alloy for battery gridsInfo
- Publication number
- WO2000000651A9 WO2000000651A9 PCT/US1999/013381 US9913381W WO0000651A9 WO 2000000651 A9 WO2000000651 A9 WO 2000000651A9 US 9913381 W US9913381 W US 9913381W WO 0000651 A9 WO0000651 A9 WO 0000651A9
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tin
- silver
- calcium
- lead
- alloy
- Prior art date
Abstract
Description
Claims