WO2000047671A1 - Low spin golf ball comprising a mantle with a cellular or liquid core - Google Patents
Low spin golf ball comprising a mantle with a cellular or liquid core Download PDFInfo
- Publication number
- WO2000047671A1 WO2000047671A1 PCT/US2000/003533 US0003533W WO0047671A1 WO 2000047671 A1 WO2000047671 A1 WO 2000047671A1 US 0003533 W US0003533 W US 0003533W WO 0047671 A1 WO0047671 A1 WO 0047671A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- golf ball
- mantle
- inches
- core
- cover
- Prior art date
Abstract
Description
Claims