WO2001015897A1 - Transparent heat-sealing film - Google Patents
Transparent heat-sealing film Download PDFInfo
- Publication number
- WO2001015897A1 WO2001015897A1 PCT/JP2000/005828 JP0005828W WO0115897A1 WO 2001015897 A1 WO2001015897 A1 WO 2001015897A1 JP 0005828 W JP0005828 W JP 0005828W WO 0115897 A1 WO0115897 A1 WO 0115897A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- heat
- film
- sealing film
- resin
- Prior art date
Abstract
Description
Claims