WO2001038415A1 - Clear coating composition having improved early hardness and water resistance - Google Patents
Clear coating composition having improved early hardness and water resistance Download PDFInfo
- Publication number
- WO2001038415A1 WO2001038415A1 PCT/US2000/031596 US0031596W WO0138415A1 WO 2001038415 A1 WO2001038415 A1 WO 2001038415A1 US 0031596 W US0031596 W US 0031596W WO 0138415 A1 WO0138415 A1 WO 0138415A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- binder
- hydroxyl
- coating composition
- component
- Prior art date
Abstract
Description
Claims