WO2001039296A1 - Multi-layer electrochemical cell devices - Google Patents
Multi-layer electrochemical cell devices Download PDFInfo
- Publication number
- WO2001039296A1 WO2001039296A1 PCT/US2000/025511 US0025511W WO0139296A1 WO 2001039296 A1 WO2001039296 A1 WO 2001039296A1 US 0025511 W US0025511 W US 0025511W WO 0139296 A1 WO0139296 A1 WO 0139296A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- separator
- electrode
- plasticizer
- layer
- cell
- Prior art date
Abstract
Description
Claims