WO2001053399A1 - Mousse de polyolefine extrudee de qualite superieure en epaisseur et panneau mousse et procede associes - Google Patents

Mousse de polyolefine extrudee de qualite superieure en epaisseur et panneau mousse et procede associes Download PDF

Info

Publication number
WO2001053399A1
WO2001053399A1 PCT/US2000/001507 US0001507W WO0153399A1 WO 2001053399 A1 WO2001053399 A1 WO 2001053399A1 US 0001507 W US0001507 W US 0001507W WO 0153399 A1 WO0153399 A1 WO 0153399A1
Authority
WO
WIPO (PCT)
Prior art keywords
foam
blowing agent
percent
propane
isobutane
Prior art date
Application number
PCT/US2000/001507
Other languages
English (en)
Inventor
Shau-Tarng Lee
Natarajan S. Ramesh
Original Assignee
Sealed Air Corporation (Us)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sealed Air Corporation (Us) filed Critical Sealed Air Corporation (Us)
Priority to CA002397599A priority Critical patent/CA2397599A1/fr
Priority to PCT/US2000/001507 priority patent/WO2001053399A1/fr
Priority to AU2000233481A priority patent/AU2000233481A1/en
Priority to EP00911611A priority patent/EP1252224A1/fr
Publication of WO2001053399A1 publication Critical patent/WO2001053399A1/fr

Abstract

L'invention se rapporte à une mousse de polyoléfine extrudée se présentant en épaisseurs d'au moins 12 mm environ, qui est dotée d'une résistance à la compression et d'une viscosité d'extension améliorées, et d'une durée de vieillissement réduite. L'invention se rapporte également à un procédé de fabrication de ladite mousse. Cette mousse est préparée à l'aide d'un agent d'expansion à base de propane. Les caractéristiques avantageuses conférées aux mousses et aux panneaux mousse de qualité supérieure en épaisseur par un agent d'expansion à base de propane peuvent être obtenues avec des quantités atteignant 75 % en volume de butane normal ou d'isopropane, ou de ces deux composés, dans l'agent d'expansion, suivant la polyoléfine sélectionnée.
PCT/US2000/001507 2000-01-21 2000-01-21 Mousse de polyolefine extrudee de qualite superieure en epaisseur et panneau mousse et procede associes WO2001053399A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CA002397599A CA2397599A1 (fr) 2000-01-21 2000-01-21 Mousse de polyolefine extrudee de qualite superieure en epaisseur et panneau mousse et procede associes
PCT/US2000/001507 WO2001053399A1 (fr) 2000-01-21 2000-01-21 Mousse de polyolefine extrudee de qualite superieure en epaisseur et panneau mousse et procede associes
AU2000233481A AU2000233481A1 (en) 2000-01-21 2000-01-21 Extruded polyolefin foam in thicker grades and plank and process therefor
EP00911611A EP1252224A1 (fr) 2000-01-21 2000-01-21 Mousse de polyolefine extrudee de qualite superieure en epaisseur et panneau mousse et procede associes

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2000/001507 WO2001053399A1 (fr) 2000-01-21 2000-01-21 Mousse de polyolefine extrudee de qualite superieure en epaisseur et panneau mousse et procede associes

Publications (1)

Publication Number Publication Date
WO2001053399A1 true WO2001053399A1 (fr) 2001-07-26

Family

ID=21740984

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2000/001507 WO2001053399A1 (fr) 2000-01-21 2000-01-21 Mousse de polyolefine extrudee de qualite superieure en epaisseur et panneau mousse et procede associes

Country Status (4)

Country Link
EP (1) EP1252224A1 (fr)
AU (1) AU2000233481A1 (fr)
CA (1) CA2397599A1 (fr)
WO (1) WO2001053399A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114940738A (zh) * 2022-06-02 2022-08-26 万华化学（宁波）容威聚氨酯有限公司 一种聚氨酯组合物、聚氨酯泡沫及其制备方法与应用

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4201763A1 (de) * 1991-01-24 1992-07-30 Astro Valcour Inc Polyolefin-schaum, diesem zugrundeliegende polymermasse sowie verfahren zur herstellung des schaums
EP0602262A1 (fr) * 1992-12-15 1994-06-22 Scriptoria N.V. Panneaux de mousse en résine de polyoléfine continus
US5801208A (en) * 1996-10-29 1998-09-01 Sealed Air Corporation Blowing agent, expandable composition, and process for extruded thermoplastic foams

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4201763A1 (de) * 1991-01-24 1992-07-30 Astro Valcour Inc Polyolefin-schaum, diesem zugrundeliegende polymermasse sowie verfahren zur herstellung des schaums
EP0602262A1 (fr) * 1992-12-15 1994-06-22 Scriptoria N.V. Panneaux de mousse en résine de polyoléfine continus
US5801208A (en) * 1996-10-29 1998-09-01 Sealed Air Corporation Blowing agent, expandable composition, and process for extruded thermoplastic foams

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114940738A (zh) * 2022-06-02 2022-08-26 万华化学（宁波）容威聚氨酯有限公司 一种聚氨酯组合物、聚氨酯泡沫及其制备方法与应用
CN114940738B (zh) * 2022-06-02 2024-02-27 万华化学（宁波）容威聚氨酯有限公司 一种聚氨酯组合物、聚氨酯泡沫及其制备方法与应用

Also Published As

Publication number Publication date
EP1252224A1 (fr) 2002-10-30
CA2397599A1 (fr) 2001-07-26
AU2000233481A1 (en) 2001-07-31

Similar Documents

Publication Publication Date Title
US5462974A (en) Expandable composition and process for extruded thermoplastic foams
US6030696A (en) Extruded polyolefin foam in thicker grades and plank and process therefor
US5801208A (en) Blowing agent, expandable composition, and process for extruded thermoplastic foams
US5527573A (en) Extruded closed-cell polypropylene foam
EP1026194B1 (fr) Mousse partiellement perforée
EP0585148B1 (fr) Mousse de polyoléfine à très basse densité, compositions de polyoléfines expansibles et procédé pour les fabriquer
AU3910297A (en) A short time frame process for producing extruded closed cell low density propylene polymer foams
US6872757B2 (en) Expandable composition, blowing agent, and process for extruded thermoplastic foams
EP1373401B8 (fr) Melanges de polymeres ethyleniques a module et consistance a l'etat fondu ameliores, et articles fabriques a partir de ces melanges
US5149473A (en) Method for production of styrenic foam
US6136875A (en) High productivity, low fugitive emission foams and foam processes
MXPA02008297A (es) Producto de espuma extruida con reducidos defectos de superficie.
EP0585147B1 (fr) Mousse de polyoléfine à base densité, compositions de polyoléfines expansibles et procédé pour les fabriquer
US20030113527A1 (en) Extruded polyolefin foam in thicker grades and plank and process therefor
CA2401943C (fr) Mousse formee d'un melange de polyethylene faible densite et de polypropylene a haute viscosite a l'etat fondu
JPH08504471A (ja) 押出し独立気泡プロピレンポリマー発泡体およびその製造法
EP1252224A1 (fr) Mousse de polyolefine extrudee de qualite superieure en epaisseur et panneau mousse et procede associes
US6299809B1 (en) Method and composition for making foamed polyethylene material
WO1999016815A1 (fr) Procede d'expansion haute productivite avec emission reduite de cov fugitif
JP2003082150A (ja) ポリ乳酸系発泡性樹脂粒子
JP3270109B2 (ja) スチレン系樹脂発泡体及びその製法
JPH1112323A (ja) 発泡用プロピレン系樹脂
JPH04272940A (ja) 発泡性粒子と発泡粒子
JP2000256497A (ja) ポリプロピレン系樹脂組成物発泡体
JPH08281762A (ja) ポリプロピレン系樹脂発泡体の製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AL AM AT AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ CZ DE DE DK DK DM EE EE ES FI FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2397599

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 2000911611

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 2000911611

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWW Wipo information: withdrawn in national office

Ref document number: 2000911611

Country of ref document: EP