WO2002010292A1 - Dual cure coating compositions having improved scratch resistance, coated substrates and methods related thereto - Google Patents
Dual cure coating compositions having improved scratch resistance, coated substrates and methods related thereto Download PDFInfo
- Publication number
- WO2002010292A1 WO2002010292A1 PCT/US2000/020839 US0020839W WO0210292A1 WO 2002010292 A1 WO2002010292 A1 WO 2002010292A1 US 0020839 W US0020839 W US 0020839W WO 0210292 A1 WO0210292 A1 WO 0210292A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- coating composition
- substrate
- composition according
- groups
- Prior art date
Abstract
Description
Claims