WO2002015251A1 - Removal of photoresist and photoresist residue from semiconductors using supercritical carbon dioxide process - Google Patents
Removal of photoresist and photoresist residue from semiconductors using supercritical carbon dioxide process Download PDFInfo
- Publication number
- WO2002015251A1 WO2002015251A1 PCT/US2000/022454 US0022454W WO0215251A1 WO 2002015251 A1 WO2002015251 A1 WO 2002015251A1 US 0022454 W US0022454 W US 0022454W WO 0215251 A1 WO0215251 A1 WO 0215251A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- solvent
- carbon dioxide
- supercritical
- supercritical carbon
- photoresist
- Prior art date
Abstract
Description
Claims