WO2002066152A2 - Adsorbent coating compositions, laminates and adsorber elements comprising such compositions and methods for their manufacture and use - Google Patents
Adsorbent coating compositions, laminates and adsorber elements comprising such compositions and methods for their manufacture and use Download PDFInfo
- Publication number
- WO2002066152A2 WO2002066152A2 PCT/US2002/000470 US0200470W WO02066152A2 WO 2002066152 A2 WO2002066152 A2 WO 2002066152A2 US 0200470 W US0200470 W US 0200470W WO 02066152 A2 WO02066152 A2 WO 02066152A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- adsorbent
- slurry
- spacers
- laminate
- laminates
- Prior art date
Abstract
Description
Claims