WO2003022900A1 - Sprayable composition for mining applications - Google Patents
Sprayable composition for mining applications Download PDFInfo
- Publication number
- WO2003022900A1 WO2003022900A1 PCT/US2002/028317 US0228317W WO03022900A1 WO 2003022900 A1 WO2003022900 A1 WO 2003022900A1 US 0228317 W US0228317 W US 0228317W WO 03022900 A1 WO03022900 A1 WO 03022900A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- dispersion
- polymer
- liner
- isocyanate groups
- bearing
- Prior art date
Abstract
Description
Claims