WO2003070138A2 - Wetness indicator having improved colorant retention - Google Patents

Abstract

A wetness indicating composition comprising a colorant disposed in a carrier matrix. The colorant provides a visible signal when activated by urine. The colorant resists leaching from the carrier matrix by being chemically bound to a component of the carrier matrix. The colorant may be bound by ionic or covalent bonds, or by intermolecular forces. The colorant may be a pH indicator. The wetness indicating composition may be incorporated into a wearable article, such as a disposable absorbent article.

Description

WETNESS INDICATOR HAVING IMPROVED COLORANT RETENTION

FIELD OF THE INVENTION This invention is directed to a wetness indicating composition having improved colorant retention and to wearable articles comprising this wetness indicating composition.

BACKGROUND OF THE INVENTION

Wearable and absorbent articles such as diapers are well known in the art. Absorbent articles typically have an absorbent core, which is held or positioned against the body of the wearer during use by a fastening system, such that the article catches the bodily exudates. Typical absorbent articles include a topsheet facing the wearer, which permits fluid exudates to pass through, and a backsheet, which prevents the exudates from escaping from the absorbent article.

Many advances have been made in the art since the introduction of the disposable absorbent article including the introduction of wetness indicating compositions associated with the inside surface of the outer cover of the article. These compositions comprise a colorant adapted to change in appearance, i.e., appear, disappear, change color, etc., upon contact with urine in the article. However, these compositions typically do not sufficiently retain the colorant within the composition, resulting in leaching of the colorant from the composition and into portions of the wearable article or onto the wearer. Certain attempts have been made in the art to retain the colorant, such as incorporating the colorant into adhesive compositions having high melting temperatures. However, the prior art fails to provide urine-indicating compositions having sufficient colorant retention performance. Thus, it would be desirable to provide wetness indicating compositions having minimal or zero leaching of the colorant from the carrier matrix. It would also be desirable to provide absorbent articles comprising these urine-indicating compositions.

SUMMARY OF THE INVENTION The present invention is directed to a wetness indicating composition comprising a colorant disposed in a carrier matrix. The colorant provides a visible signal when activated by urine. The colorant resists leaching from the carrier matrix by being chemically bound or by being bound by intermolecular forces to a component of the carrier matrix.

BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 shows a plan view of a disposable diaper embodiment of the present invention. Figure 2 shows a section view of a portion of the disposable diaper of Figure 1. Figure 3 shows a plan view of an alternative disposable diaper embodiment of the present invention.

Figure 4 shows a plan view of another alternative disposable diaper embodiment of the present invention.

Figure 5 shows a section view of a portion of the disposable diaper of Figure 4.

Figure 6 shows a graph of pH indicator leaching at various exposure times.

Figure 7 shows a bar graph of pH indicator leaching at various exposure times.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is directed to a wetness indicator that may, for example, be used in conjunction with a wearable article, including but not limited to disposable absorbent articles. As used herein, the term "wearable article" refers to articles adapted to be applied or affixed to, or otherwise associated with a portion of a wearer's anatomy for a certain period of time, and often during a wearer's normal activities. Wearable articles may encircle or at least partially enclose a portion of a wearer's body, such as in the case of belts, diapers, training pants, underwear, and the like. Such wearable articles may include elasticically extensible and or fastening components to ensure a proper fit to the wearer and/or fastening components to provide for convenient application and removal of the article from the wearer by a caregiver. Alternatively, in addition to the above-described features, at least a portion of the wearable article may be adhesively affixed to the skin of the wearer. In some embodiments, the wearable article may include a separate element, such as an insert, affixed to or associated with the wearable article. Alternatively, the wearable article may comprise an insert adapted to be attached to or associated with a durable or semi-durable article of clothing, such as underwear or a diaper cover. Although not limited to such embodiments, the present invention will generally be described below as associated with a disposable absorbent article.

As used herein, the term "absorbent article" refers to devices, which absorb and contain body exudates and, more specifically, refers to devices that are placed against or in proximity to the body of the wearer to absorb and contain the various exudates discharged from the body. The term "disposable" is used herein to describe absorbent articles that generally are not intended to be laundered or otherwise restored or reused as absorbent articles, i.e., they are intended to be discarded after a single use and, preferably, to be recycled, composted or otherwise discarded in an environmentally compatible manner. A "unitary" absorbent article refers to absorbent articles which are formed of separate parts united together to form a coordinated entity so that they do not require separate manipulative parts like a separate holder and/or liner. A preferred absorbent article embodiment of the present invention is the unitary disposable absorbent article, diaper 20, shown in Figure 1. As used herein, the term "diaper" refers to an absorbent article generally worn by infants and incontinent persons about the lower torso. The present invention is also applicable to other wearable and absorbent articles such as incontinence briefs, incontinence undergarments, absorbent inserts, diaper holders and liners, feminine hygiene garments, bandages and the like. Figure 1 is a plan view of the diaper 20 of the present invention in a flat-out, state with portions of the structure bemg cut-away to more clearly show the construction of the diaper 20 The portion of the diaper 20, which faces the wearer, is oriented towards the viewer As shown in Figure 1, the diaper 20 preferably comprises a liquid pervious topsheet 24, a liquid impervious backsheet 26, an absorbent core 28 that is preferably positioned between at least a portion of the topsheet 24 and the backsheet 26, side panels 30, elasticized leg cuffs 32, an elastic waist feature 34, and a fastening system generally designated 40 The diaper 20 is shown in Figure 1 to have a first waist region 36, a second waist region 38 opposed to the first waist region 36 and a crotch region 37 located between the first waist region 36 and the second waist region 38 The periphery of the diaper 20 is defined by the outer edges of the diaper 20 in which longitudinal edges 50 run generally parallel to the longitudinal center ne 100 of the diaper 20 and end edges 52 run between the longitudinal edges 50 generally parallel to the lateral centerhne 110 of the diaper 20

While the topsheet 24, the backsheet 26, and the absorbent core 26 may be assembled in a variety of well-known configurations, preferred diaper configurations are described generally in U S Pat No 3,860,003 entitled "Contractible Side Portions for Disposable Diaper" issued to Kenneth B Buell on January 14, 1975, U S Pat No 5,151,092 issued to Buell on September 9, 1992, and U S Pat No 5,221,274 issued to Buell on June 22, 1993, and U S Pat No 5,554,145 entitled "Absorbent Article With Multiple Zone Structural Elastic-Like Film Web Extensible Waist Feature" issued to Roe et al on September 10, 1996, U S Pat No 5,569,234 entitled "Disposable Pull-On Pant" issued to Buell et al on October 29, 1996, U S Pat No 5,580,411 entitled "Zero Scrap Method For Manufacturing Side Panels For Absorbent Articles" issued to Nease et al on December 3, 1996, and U S Patent No 6,004,306 entitled "Absorbent Article With Multi-Directional Extensible Side Panels" issued to Robles et al on December 21, 1999, each of which is incorporated herem by reference

The backsheet 26 is generally that portion of the diaper 20 positioned adjacent garment facing surface 45 of the absorbent core 28 that prevents the exudates absorbed and contained therein from soiling articles that may contact the diaper 20, such as bedsheets and undergarments The topsheet 24 is preferably positioned adjacent body facing surface 47 of the absorbent core 28 and may be joined thereto and/or to the backsheet 26 by any attachment means known m the art As used herem, the term "joined" encompasses configurations whereby an element is directly secured to another element by affixing the element directly to the other element, and configurations whereby an element is indirectly secured to another element by affixing the element to intermediate member(s) that m turn are affixed to the other element The topsheet 24 is preferably compliant, soft-feelmg, and non-irritating to the wearer's skm Further, at least a portion of the topsheet 24 is liquid pervious, permitting liquids to readily penetrate through its thickness

The absorbent core 28 may comprise any absorbent material which is generally compressible, conformable, non-irritating to the wearer's skin, and capable of absorbing and retaining liquids such as urine and other certain body exudates The absorbent core 28 may be manufactured in a wide variety of sizes and shapes and may compnse a wide variety of liquid-absorbent materials commonly used in disposable diapers and other absorbent articles such as comminuted wood pulp, which is generally referred to as airfelt Examples of other suitable absorbent materials mclude creped cellulose waddmg, meltblown polymers, including coform, chemically stiffened, modified or cross-linked cellulosic fibers, tissue, including tissue wraps and tissue lammates, absorbent foams, absorbent sponges, superabsorbent polymers, absorbent gelling materials, or any other known absorbent material or combinations of materials

As noted above, the diaper 20 may also mclude a fastening system 40 The fastening system 40 preferably maintains the first waist region 36 and the second waist region 38 m a configuration so as to provide lateral tensions about the circumference of the diaper 20 to hold the diaper 20 on the wearer The fastening system 40 preferably comprises a surface fastener such as tape tabs, hook and loop fastening components and/or hermaphroditic fastening components, although any other known fastening means are generally acceptable In alternative embodiments, opposmg sides of the article may be seamed or welded to form a pant This allows the article to be used as a pull-on type diaper, such as a training pant

Caregivers frequently desire to know whether urme is present m an absorbent article, such as a diaper, and/or how much urme is present This may be due to health concerns, e g , whether the child is getting enough fluid, or skm health/containment concerns, e g , whether the diaper contams sufficient urme to warrant changmg The presence of urme may be signaled to the caregiver as a color or contrast change detectable m at least a portion of the article and visible prior to removal of the article, e g , through the outer cover of the article, by a wetness indicator, which is termed a "urme indicator" in this usage Colorants, such as food grade dyes and pH indicators that change color when wetted with urme, may be used m this context The art describes a number of urme or wetness indicator approaches employmg these types of colorants, including their incorporation mto the absorbent core or application to, or association with, the inside surface of the backsheet One common approach, including a material used in currently marketed PAMPERS™ diapers in Japan, is to formulate a hot melt adhesive containing a small quantity of a pH indicator These materials are known as hot melt wetness indicators (HMWI)

The primary issue with HMWIs and the other colorant based wetness mdicators described in the art is the tendency of the colorant to leach from the carrier matrix A carrier matrix is a quantity of a material or materials serving to hold or retain the wetness indicator m the desired position within the product, such that urme will come into contact with it and such that a physical change in the wetness indicator, such as a change in color, will be sensible to the wearer or a caregiver In certain embodiments of the present invention, components of the carrier matrix can also contribute to reduced leaching of the colorant due to the formation of intermolecular binding forces Excess urme may cause the colorant to diffuse out of, l e , leach from, the earner matrix and migrate toward and possibly through the backsheet and/or topsheet This may lead to consumer negatives such as clothing or beddmg staining, and/or may cause the wetness indicator to appear unsightly through the backsheet, l e , the applied pattern of the wetness indicator composition may become blurry, indistinct, or otherwise aesthetically displeasing Wetness indicators resistant to leaching of the colorant from the matrix are highly desirable, therefore, to minimize concerns related to colorant migration within, or out of, the article Preferred wetness indicating compositions are highly resistant to colorant leaching, as described above, and are resistant to premature activation in high humidity environments, which may render the wetness indicator less effective in detecting and/or indicating the presence of urine in a wearable article. For instance, exposure to a high level of humidity may partially activate wetness indicating compositions that are not highly resistant to colorant leaching and thereby make any color change in the presence of urine less noticeable. Additionally, preferred wetness indicating compositions should have excellent signal clarity and kinetics, i.e., the signal should be visible soon after contact with urine.

The wetness indicators of the present invention generally comprise at least one colorant disposed in a carrier matrix. The colorant is activatable by urine, i.e., the colorant may change in color, appear, disappear, or change in intensity or visual distinctiveness in response to contact with urine or a component thereof. The carrier matrix comprises one or more components that may facilitate the incorporation of the wetness indicator composition into a finished product, such as a wearable article, and/or retain the colorant during initial placement or during use. Upon contact with urine, the carrier matrix preferably allows sufficient urine to contact the colorant and effect a change in appearance while preventing the colorant, in either its virgin or activated state, from leaching out of the carrier matrix into the surrounding environment, such as the absorbent core of a wearable article. The wetness indicator of the present invention may be incorporated into the article in any desired pattern or configuration, including, but not limited to, stripes, dots, geometric shapes, alphanumeric characters, pictorial representations of animate or inanimate objects, or any combination or arrangement thereof.

Urine contacting the wetness indicator at least partially diffuses into the carrier matrix where it contacts the colorant. If the colorant is a pH indicator, contact with urine having a higher pH than the indicator threshold results in a color change, e.g., yellow to blue, etc. If the colorant is a food grade dye, contact with urine may solubilize the dye, enabling it to bloom within or to the surface of the carrier matrix, resulting in an intensification of the dye's color.

Some pH indicators are neutral in charge and lightly colored at acidic pH's. For example, bromocresol green, bromocresol purple, and bromophenol blue are all neutrally charged and yellow in color at an acidic pH. As the pH exceeds the pK_a of the indicator, a charge and related color change occurs. For example, bromophenol blue changes from a yellow neutral state to an anionic blue state at a pH greater than its pK_a of approximately 4.0.

In these embodiments, the pH indicator is incorporated into the carrier matrix in its neutral acid form. The neutral charge of the pH indicator allows it to be more easily solubilized into hydrophobic systems. Upon contact with urine, which typically has a pH in the range of 5.5 to 8.0, the indicator changes color, e.g., from yellow to blue. In addition to the color change, the charge on the pH indicators also changes from neutral to anionic at pH values above its pKa value. This negative charge on the pH indicator not only causes the dye molecule to change color, but the more polar nature of the anion also enhances the solubility and leaching of the dye into an aqueous environment. In certain embodiments of the present invention, incorporating the colorant, 1 e , mdicator or dye, into a hydrophobic matrix that preferentially "locks" the molecule into the matrix may inhibit the leachmg of the aniomc colorant mto the urme In these embodiments the amomc colorant may become preferentially absorbed mto the matrix due to intermolecular bonding forces Some of the types of intermolecular forces responsible for inhibiting the leachmg of the colorant mto the urme mclude hydrogen bonding, electrostatic forces, van der Waals forces and hydrophobic mteractions Thus, even though the charged portion of the colorant in its virgin state would be hydrated by water m the urme, leaching of the colorant may be inhibited due to intermolecular bonding forces between the materials of the matrix and the colorant

However, m preferred embodiments of the present invention, the colorant is chemically bound to at least one component of the carrier matrix, such as a catiomc species Chemical bonds mclude covalent, ionic, and metallic bonds In embodiments wherem the earner matrix comprises a catiomc species, the catiomc species may function as a leaching inhibitor to reduce or completely elimmate leachmg of an amomc dye colorant from the carrier matrix In particular, leachmg of the amomc dye indicator is preferably inhibited via addition of a permanently charged catiomc molecule m the wetness indicator composition For example, quaternary ammonium compounds are particularly effective leachmg inhibitors by inhibiting colorant leachmg from the matrix and enhancing the contrast and clanty of the wetness mdicator pattern Without wishing to be bound by theory, we believe the catiomc quaternary ammonium compound forms an lonically bonded coacervate with the negatively charged pH indicator due to the strong coulombic mteraction between the amomc dye and the catiomc quaternary ammonium compound The coacervate complex formed between the amomc dye and catiomc quaternary ammonium compound neutralizes the charge m both species and dramatically reduces both of their solubilities in polar solvents such as water or urme, thereby dramatically lnhibitmg leaching of the colorant from the carrier matrix The intermolecular forces between the coacervate and the carrier matrix, as described above, may further limit the diffusion and mobility of the colorant mto an aqueous environment such as urme

This leaching inhibition is particularly beneficial m locking the pH mdicator or dye directly within the wetness indicator on the backsheet rather than allowing free diffusion of the dye or mdicator through the diaper core and possibly contaminating the diaper topsheet In addition, a clearer and more distmct wetness mdicator pattern may be produced in embodiments wherem dyes or pH indicators are locked mto the matrix As noted, dyes or pH indicators that diffuse out of the wetness mdicator pattern tend to appear blurred and less distmct

In certain embodiments of the present invention, the addition of the quaternary ammonium compound may also function to darken the color change of sulfonephthalein pH mdicators, especially those belongmg to the sulfonephthalein class of pH indicators Without wishing to be bound by theory, we believe this may be attributed to several possible factors 1) alkaline impurities within the quaternary ammonium raw material, 2) absorption shiftmg and absorptivity coefficient increases due to coacervate formation and, or 3) mcreased amomc dye formation For example, the alkaline impurities possibly result m a more basic environment surrounding the dye Therefore at the higher pH, greater concentrations of blue anionic dye species are formed and a darker color results. Additionally, the coacervate formed between the anionic pH indicator and the cationic quaternary ammonium compound may cause an absorption spectral shift and absorptivity coefficient increase such that the dye is more darkly colored when associated to the cationic species. Finally, the coacervate formation may cause a concomitant decrease in the anionic dye species concentration after contact with urine. This decrease in the anionic species concentration can cause a shift in the equilibrium such that more amonic dye species are formed via the Le Chatelier Principle. This higher concentration of the blue anionic dye indicator leads to a darker blue color. Of course, the darker blue color may be the result of any combination of these phenomena.

As previously described, the cationic quaternary ammonium compound is believed to reduce leaching of the anionic dye via formation of an insoluble coacervate. Alternatively, it is possible to inhibit leaching of a cationic dye or cationic pH indicator by incorporating an anionic compound into the carrier matrix of the wetness indicator. For example, many polyacrylic acid polymers and organic acids such as stearic acid are negatively charged at pH's above approximately 5. If the pH indicator undergoes a transition to a cationic species at the typical urine pH of 5.5 to 8.0, the formation of an insoluble coacervate may occur, inhibiting leaching in a manner similar to the systems described above.

The carrier matrix may comprise components that modify the relative hydrophilicity/hydrophobicity (HLB ratio), modify the melting point of the wetness indicating composition, change the flexibility of the indicating composition, enhance the adhesion to the backsheet material, affect the leaching of the colorant, and/or alter the humidity resistance of the composition. For instance, some waxes increase the flexibility and hydrophobicity of the composition while also increasing the adhesive tack to the backsheet. Some waxes also reduce the leaching of the colorant into aqueous environments due to intermolecular binding forces. Non-limiting examples of suitable natural and synthetic waxes include highly branched waxes, such as microcrystalline waxes, paraffin waxes, polyethylene waxes, polyethylene glycol type waxes, silicone waxes, beeswax, ozokerite, ceresin, and carnauba wax.

Linear primary alcohols, such as stearyl alcohol, may be added to the carrier matrix and may function as co-emulsifiers and enhance the composition stability. The carrier matrix may comprise any composition that may be applied to a substrate, i.e., a structural component of the article such as the backsheet, the topsheet, or the absorbent core of an absorbent article, in preferably a liquid form that at least partially solidifies after application to the substrate. Preferably, the solidification of the composition onto the backsheet substrate is relatively rapid to avoid potential transfer and loss of the composition to other regions of the article and/or processing equipment.

If the carrier matrix is an emulsion or solution, solidification may occur via the evaporation of a solvent such as water or other safe solvent. In preferred embodiments of the wetness indicating composition of the present invention, the carrier matrix is a meltable composition and solidifies, i.e., achieves a solid or semi-solid physical state, rapidly via cooling. In certain embodiments, the inclusion of crystalline materials such as paraffin waxes can increase the solidification rate of the composition. The carrier matrix may be an adhesive or other meltable composition having a melting point above room temperature, such as a skin care composition or a component thereof. Exemplary skin care compositions are described in U.S. Patents 5,607,760; 5,609,587; 5,635,191; 5,643,588; 6,118,041; 6,107,537; and 5,968,025, incorporated herein by reference.

Carrier matrices may include components such as waxes, e.g., microcrystalline, paraffm, natural, synthetic, polyethylene type, polyethylene glycol type, silicone type, etc., surfactants such as ethoxylated alcohols, fatty alcohols, high molecular weight alcohols, esters, polymers, and any other natural or synthetic waxes or olefϊnic materials as known in the art. Optionally, the carrier matrix may also include viscosity increasing agents and/or hardening agents. Suitable examples of viscosity increasing agents include polymeric thickeners such as block copolymers having polystyrene blocks on both ends of a rubber molecule, copolymers of ethylene and vinyl acetate, hydrogenated castor oil, polymers, metal salts of fatty acids, silicas and/or derivatized silicas, organoclays such as the modified and unmodified hectorites and bentonites, modified clays such as modified laponite clays, dibenzylidene sorbitol, alkyl galactomannan, aluminum magnesium hydroxide stearate/oil blends, and lauroyl glutamic dibutylamide. Hardening agents may include the aforementioned waxes, C14-22 fatty alcohols, C23-60 alcohols, C14-22 fatty acids, C23-60 carboxylic acids, hydrogenated vegetable oils, polymers, sorbitan esters, and other high molecular weight esters.

The colorant preferably is attracted to the carrier matrix or a component thereof, and forms ionic or covalent bonds therewith, i.e., is ionically or covalently bound thereto. As previously described, the carrier matrix may comprise a cationic species capable of forming ionic bonds with anionic colorant molecules, such as activated pH indicators, thereby significantly reducing the possibility of the colorant leaching from the wetness indicator composition. Other suitable leaching inhibitor materials include cationic clay materials, such as sodium montmorillonite, that may attract and ionically bind anionic colorants, such as activated pH indicators as described herein. Other clays with known anionic binding capacity, i.e., cationic clays, include beidellite, nontronite, saponite, vermiculite, kaolinite, and clays reacted with quaternary compounds such as tetramethylammonium chloride, and polyquarternized amines.

Alternatively, the colorant may be covalently bound to at least one component of the carrier matrix. For example, the dye or pH indicator may be functionalized onto a polymer backbone such that the dye or pH indicator is covalently bound to the polymer. Specifically, the sulfonephthalein class of pH indicators may be covalently coupled to amine and hydroxyl containing materials via cyanuric chloride activation. Examples of amine containing materials that can be coupled to the sulfonephthalein indicators via cyanuric chloride include chitosan, polyethyleneimines, polyamines and polyacrylamides. The cyanuric chloride coupling reagent may also be used to couple the colorant to hydroxyl containing molecules or polymers such as cellulose and polyethylene glycols. To inhibit the solubility of the coupled complex in an aqueous liquid such as urine, hydrophobic water insoluble functionalities such as long alkyl chains may be derivatized onto the colorant or polymer backbone via any means known in the art. Other coupling reagents that may be used to covalently bind the colorant to a component of the carrier matrix include carbodiimides that can link carboxyl moieties to amine moieties, glutaraldehyde that can link amine functionalities to one another, cyanogen bromide that can link hydroxyl groups to amine moieties, and hydrazine that can link amides to aldehyde functionalities.

In certain alternate embodiments, the carrier matrix may comprise at least one component in which the colorant is substantially soluble and for which the colorant has a strong affinity. For example, the carrier matrix may include a component having an aromatic group to which the pH indicator's aromatic group has an affinity. For example, the carrier matrix may include a material having a styrene moiety, such as a styrene block copolymer, e.g., a styrene-butadiene, or SBS, copolymer, and the pH indicator may comprise bromophenol blue. Since both molecules contain aromatic ring hydrocarbons, there are intermolecular forces that can aid in inhibiting the dye leaching effect. In another example, the carrier matrix may comprise a clay material for which the colorant has an affinity. For instance, modified organoclay hectorite rheological additives contain long alkyl chains that may interact with dyes and indicators containing alkyl chains, reducing the tendency of the colorant to leach from the carrier matrix. As noted, such materials as waxes and linear primary alcohols incorporated in the carrier matrix can also reduce the leaching of the colorant through these intermolecular forces of attraction.

The carrier matrix preferably includes a surfactant to provide or enhance both composition phase stability and wettability. Surfactants comprise both polar and hydrophobic moieties. Because of this unique structure, they facilitate the stabilization of compositions containing both polar and hydrophobic ingredients. For example, surfactants employed in this invention allow for the mixing and stabilization of polar quaternary ammonium compounds with microcrystalline waxes. In addition to facilitating the mixing of dissimilar materials, the inclusion of the surfactant may also increase the speed of the color change of the pH indicator after urine contacts the composition. Since these compositions may contain relatively high concentrations of hydrophobic ingredients such as waxes and linear primary alcohols, the wettability of such a matrix with urine is often nonoptimal, preventing the pH indicator from being wetted out and changing color at a desirable rate. For this reason, surfactants are preferably added to the wetness indicating compositions of the present invention to enhance the wettability of the composition. For example, non-ionic surfactants such as ethoxylated alcohols effectively enhance the wettability of many wetness indicating compositions, allowing the color of the wetness indicator to change in less than about five minutes. Non- limiting examples of other surfactant classes that may also improve stability and wettability include anionic and cationic surfactants, alkoxylated alkylates such as PEG-20 stearate, end group-capped alkoxylated alcohols, alkoxylated glyceryl and polyglyceryl alkylates such as PEG-30 glyceryl stearate, glyceryl alkylates such as glyceryl stearate, alkoxylated hydrogenated castor oil, alkoxylated lanolin and hydrogenated lanolin, alkoxylated sorbitan alkylates, sugar derived surfactants such as the alkyl glycosides and sugar esters, poloxamers, polysorbates, and sulfo succinic acid alkyl esters.

Preferably, the concentrations and structures of each of the components within the indicating composition are preferably concurrently optimized for several important properties: 1) rriinimal colorant leaching, 2) high contrast color change, 3) rapid color change kinetics, 4) stability to humidity during storage, 5) adhesion to the backsheet, 6) ease of processing, and 7) low cost. As noted above, in certain preferred embodiments colorant leachmg inhibition may be due predominately to the formation of the neutrally charged coacervate between a catiomc species, such as a quaternary ammonium compound, and an amomc activated colorant As described above, inclusion of a hydrophobic wax, lmear primary alcohol, or aromatic containing matenal into the carrier matrix may aid in locking this coacervate and colorant mto the matrix In certain embodiments, the wax, lmear primary alcohol, or aromatic containing material may also contribute to enhanced stability m high humidity environments

The inclusion of acidic materials also plays an important role m stabilizing the system to premature color changes caused by exposure to humid environments The inclusion of the acidic materials helps mamtam a low pH environment around the pH mdicator even when the system is exposed to high humidities This mamtenance of a low pH environment keeps the pH mdicator m its neutral and lightly colored state Acids which are particularly effective in stabilizing the wetness mdicator formula to high humidities include organic acids such as monostearyl phosphate, citrate esters such as monostearyl citrate, glycolate esters, lactate esters, fatty acids such as stearic and palmitic acid, ether carboxy c acids, N-acyl sarcosinic acid surfactants, N-acyl glutamic acid surfactants, N-acyl ethylenediaminetnacidic acid surfactants, alkane sulfomc acids, alpha-olefin sulfomc acids, alpha-sulfomc acid fatty acid methyl esters, sulfate esters, fruit acids such as citric acid, salicylic acid, and inorganic acids such as phosphoric acid

The addition of too much acid or hydrophobic materials withm the carrier matrix may inhibit both the intensity of the color change and the kinetics of this change Thus, it is important to carefully balance the amount of each of the ingredients m the formula to optimize the properties of the wetness mdicator composition As noted, another important mgredient in these formulas is the inclusion of a wetting agent In this case, ethoxylated alcohols have been found to be particularly effective The role of the wetting agent is to mcrease the speed of the color change kinetics and to enhance the stability of the fully formulated mixture Smce a material such as a hydrophobic wax and a charged quaternary ammonium compound may be incompatible, the inclusion of an ethoxylated alcohol surfactant, which possesses both hydrophobic and hydrophilic moieties, helps bridge these incompatible materials into a stable matrix Addition of linear alcohol and carboxyhc acid co-emulsifiers such as stearyl alcohol and behenyl alcohol may also function to enhance the stability and wettability of these systems

For urme indicating compositions comprising a leaching inhibitor, such as a quaternary ammonium compound, the colorant leachmg inhibition is greatest for amomc colorants due to the strong attraction between the catiomc leachmg inhibitor and the amonic activated colorant, as described above The sulfonephthalein class of pH indicators are particularly preferred colorants In an acidic state, the sulfonephthalein class of indicators have a "neutral" charge and are typically yellow m color The neutral charge enhances the solubility of these pH mdicators m relatively hydrophobic carrier matrices as described above Upon contact with urme having a pH higher than their pK_a, the sulfonephthalein class of pH indicators typically change to a blue-green color and have an anionic charge, allowing the pH indicator to be scavenged by the catiomc quaternary ammonium compound Examples of suitable sulfonephthalein pH indicators include bromocresol green, bromocresol purple, m-cresol purple, cresol red, chlorophenol red, bromothymol blue, bromopyrogallol red, bromoxylenol blue, and bromophenol blue.

Other examples of pH indicators and dyes which are neutral in their acidic state and anionic after contact with urine include monoazo dyes such as acid alizarin violet N, monoazo pyrazolone dyes such as acid yellow 34, diazo dyes such as acid black 24, acid anthraquinone dyes such as acid black 48 and alizarin complexone dihydrate, amphoteric anthraquinone dyes such as acid blue 45, triphenylmethane dyes such as acid fuchsin, phthalein type dyes such as o-cresolphthalein, and xanthene dyes such as 2',7'- dichlorofluorescein and eosin B.

Alternatively, a cationic dye or cationic pH indicator may be scavenged with an anionic leaching inhibitor. Dyes and/ or pH indicators that are neutral in their basic state and cationic after contact with urine include heterocyclic acridine aromatics such as acridine and acridine orange, diphenylmethane dyes such as auramine O, triphenylmethane dyes such as basic fuchsin, cationic thiazine dyes such as azure C, cationic anthraquinone dyes such as basic blue 47, and phthalocyanine type dyes such as copper phthalocyanine. Permanently charged cationic dyes and pH indicators that may be scavenged by an anionic leaching inhibitor include quaternized phthalocyanine type dyes such as alcec blue and cationic polymethine dyes such as astrazon orange G. Neutral dyes and pH indicators that may be bound to the matrix due to intermolecular forces described above include anthraquinone type such as alizarin, the neutral complex dyes such as azure A eosinate, and the terpene type such as trans-beta-carotene.

As described above, when a neutral acidic, i.e., anionic when activated, pH indicator contacts urine having a pH greater than its pK_a, the indicator changes color and assumes an anionic charge, i.e., the indicator is "activated." In preferred embodiments including a cationic species as a leaching inhibitor, the leaching inhibitor is preferably a cationic quaternary ammonium compound adapted to associate with the activated anionic form of a pH indicator, especially the sulfonephthalein class of pH indicators. The dialkydimethylammonium quaternary compounds are especially effective in reducing the leaching of anionic dyes or pH indicators. Suitable examples mclude dicocoalkyldimethlyammonium chloride, di(hydrogenated tallowalkyl)dimethlyammonium chloride, and distearyldimethylammonium chloride. An especially preferred cationic quaternary ammonium compound is 2- ethymexymydrogenatedtallowalkyldimethlyammonium methyl sulfate. Alkyltrimethylammomum chlorides may also in some embodiments, function as leaching inhibitors. Examples include dodecyltrimethylammonium chloride, hexadecyltrimethylammonium methylsulfate, and octadecyltrimethylammonium chloride. Other classes of cationic quaternary ammonium salts that may act as leaching inhibitors include the imidazoline quaternary class, the mono-, di-, tri- and terra- amidoamine quaternary class, the mono-, di-, tri- and terra- alkyl quaternary class, the mono-, di-, tri- and terra- benzyl quaternary class, the benzylalkyl quaternary class of cationic compounds, the cationic diquaternary class, and the cationic ethoxylated quaternary class. Finally, it should be noted that the counter anion used in neutralization of the cationic quaternary compound is not specifically limited to chloride. Other anions can also be employed and non-limiting examples include methyl sulfate and nitrite. Other catiomc materials that would likely be useful aids m the inhibition of leachmg mclude amine acid salts, polyacryamidopropyltrrmmomum chlonde, PEG-2 dimeadowfoamamidoethylmonium methosulfate, meadowfoam glyceryl quatermum, alkyl betames, alkyl amido betaines, irmdazolmium betaines, sulfobetaines, quaternrzed poly(vιnylpyπdιne), amidoamine acid salts, poly(ιmrne) acid salts, polyethylene m me acid salts, catiomc polyacryamides, poly(vιnylamιne) acid salts, catiomc lonene polymers, poly(vιnylbenzyl onium salts), poly(vmylunιdazolmιum salts), quatermzed silicone compounds such as the diquaternary polydimethylsiloxanes, poly(vιnyl alcohol) quaternary materials, catiomc guars, polydimethyldiallylammomum chloride, catiomc and aniomc exchange resms and polymers, copolymers of vinylpyrrohdone and methyacrylamidopropyltnmethylammonium chloride, acidified polyvmylpyrrohdones, acidified polyvinylpolypyrrolidones, acidified copolymers of vinylpyrrohdone and vmylacetate, acidified copolymers of vinylpyrrohdone and dimethylammoethylmetacrylate, copolymers of vinylpyrrohdone and methacrylamidopropyl trimethlyammomum chloride, copolymers of quatermzed vinylpyrrohdone and dimethylaminoethylmethacrylate, acidified vmylcaprolactam based polymers, acidified copolymers of vinylpyrrohdone and styrene, acidified copolymers of vinylpyrrohdone and acrylic acid, catiomc polyelectrolyte polymers, and acidified n-alkyl-2-pyrrolιdones

It should be noted that the amines previously mentioned can be rendered cationic via several different approaches One means of converting the amine mto a catiomcally charged species is via contact with the urme itself smce amines are protonated at the typical urme pH range of 5 5 to 8 0 In addition, the acid salt of the amine can be prepared prior to formulating mto the composition by acidification with an acid or acids A variety of morgamc and orgamc acids can be used for this purpose Examples mclude orgamc acids such as citric acid and adipic acid while inorganic acid examples include phosphoric acid and hydrochloric acid These acidified armne salts could also be formulated into the composition as supplied m the acid form from the manufacturer

As noted previously, the ionic bond formed between the catiomc colorant inhibitor and the aniomc colorant leads to a hydrophobic coacervate upon neutralization of the charge in both species Bemg hydrophobic, the solubility of the coacervate is very low m hydrophilic liquids such as urine In addition, the solubility m urine is further limited due to the intermolecular forces between the coacervate and the carrier matrix and other components withm the carrier matrix For example, stearyl contaming catiomc quaternary ammonium salts can form the coacervate with the activated amonic bromocresol green The stearyl groups within the coacervate interact through intermolecular binding forces with other stearyl moieties m the carrier matrix For instance, the orgamc acids of monostearyl phosphate and monostearyl citrate would be expected to form intermolecular forces of attraction with the stearyl containing coacervate In addition, stearyl alcohol and the alkyl groups of many waxes would also be be expected to form intermolecular forces of attraction with the stearyl containing coacervate

Thus, coacervate formation is the preferred mode in inhibiting leaching of the colorant mto the aqueous urine But, it is not required for inhibiting leachmg of the colorant Compositions without cationic materials necessary to form the coacervate have also exhibited reduced leaching As noted, this is due to intermolecular forces binding the activated anionic colorant within the carrier matrix. For example, hydrophobic regions within the molecular structure of the colorant can interact with both hydrophobic carrier matrix materials and components formulated into the carrier matrix.

The amount of colorant leaching was measured in systems where both ionic bonding lead to coacervate formation and where only intermolecular forces lead to inhibiting leaching. Ideally, the amount of colorant leaching is inhibited completely such that no colorant is detected in urine or other aqueous test solvents such as synthetic urine. In some embodiments, πiinimal colorant leaching is acceptable since the wetness indicator pattern is maintained with superior sharpness and color contrast. In addition, minimal colorant leaching does not lead to contamination of the diaper's topsheet. The amount of leaching in each of these compositions was measured by using the Leaching Value Test Methods described in detail below. For 20 minutes of exposure to the synthetic urine composition, the wetness indicators of the present invention preferably have a 20 Minute Leaching Value of less than 300 micrograms of colorant leached per gram of wetness indicator (see bar 90 in figures 6 and 7 below) and most preferably less than 100 micrograms of colorant leached per gram of wetness indicator (see bar 92 in figures 6 and 7 below) as measured via the 20 Minute Leaching Value Test Method described in detail below. The 20 Minute Leaching Value is defined as the micrograms of colorant leached per gram of wetness indicator during exposure to synthetic urine for twenty minutes. For 3 hours of exposure to the synthetic urine composition, the wetaess indicators of the present invention have a 3 Hour Leaching Value of less than 600 micrograms of colorant leached per gram of wetness indicator (see bar 94 in figures 6 and 7 below), preferably less than 300 micrograms of colorant leached per gram of wetness indicator (see bar 96 in figures 6 and 7 below), and most preferably less than 100 micrograms of colorant leached per gram of wetaess indicator (see bar 98 in figures 6 and 7 below). The 3 Hour Leaching Value is defined as the micrograms of colorant leached per gram of wetaess indicator after exposure to the synthetic urine for three hours. The details for the measurement for both the 20 Minute Leaching Value and the 3 Hour Leaching Value are given below in the sections describing the 20 Minute Leaching Value Test Method, the 1 Hour Leaching Value Test Method, the 3 Hour Leaching Value Test Method, and the 14 Hour Leaching Value Test Method.

20 Minute Leaching Value Test Method

The 20 Minute Leaching Value is measured using the following 20 Minute Leaching Value Test Method. Cut out a 38 mm diameter circular piece of diaper backsheet material using a circular die tool. A nonlimiting example of a backsheet material is microporous polyethylene with a basis weight of 37 grams per square meter as available from Tredegar Industries, Richmond, VA, U.S.A.. Weigh this blank circular backsheet sample on an analytical balance accurate to at least four decimal places. Record this weight.

Heat and magnetically stir the wetness indicator formulation on a hot plate until it reaches a temperature of 95-100°C. Using a wooden tongue depressor or metal spatula, apply a thin coating of the molten mine indicator material onto the circular diaper backsheet material such that the total weight of the wetness indicator composition on the disk is between 0.03 g and 0.15 g. The entire surface of the backsheet sample should be covered with a substantially uniform film of the wetaess indicator as judged by its visible appearance to the naked eye. Discard sample if the entire surface of the backsheet sample is not covered or if the film is substantially non-uniform. Weigh and record the total weight of each wetaess indicator coated backsheet disk. Calculate and record the weight to the ten-thousandth place of the wetaess indicator applied to each backsheet disk. Discard any samples that do not fall between 0.03 g and 0.15 g of total wetaess indicator deposited onto the backsheet sample.

Using a nitrile gloved index finger cover, apply approximately 0.05 g to 0.15 g of a tacky microcrystalline wax (MULTIWAX™ W-835 or equivalent) at a temperature of 20°C to the bottom of a 60 ml, 50 mm diameter glass sample jar. Spread the microcrystalline wax on the inside base of the jar so it encompasses an area approximately 12 mm in diameter in the center of the inside base of the jar.

Carefully place the wetness indicator coated backsheet disk onto the microcrystalline wax in the center of the inside base of the glass jar. The wetaess indicator coated side should face up. Using a nitrile gloved index finger, carefully press the backsheet sample into the wax such that the sample sticks to the base of the jar.

Prepare a synthetic urine composition by weighing and dissolving the following ingredients in 5000.0 grams of distilled water:

Heat and magnetically stir the synthetic urine composition on a hot plate until it reaches a temperature of 37-39°C and the mixture is clear, transparent, and colorless with no signs of particulate matter. Keep covered to avoid evaporation of the water. Add 20.0 g of this heated synthetic urine to the sample jar containing the wetaess indicator sample disk. Tightly seal the jar with its lid and shake up and down ten times. Shake with a frequency of approximately two cycles per second and an amplitude of approximately 25 cm. Allow the jar to sit at ambient conditions of approximately 20°C and 1 bar for 20 minutes. For this 20 minute exposure time and all other exposure times, eight replicates for each unique wetness indicator composition should be tested using this 20 Minute Leaching Value Test Method.

After the test time interval has elapsed, shake the jar up and down an additional 5 times (same amplitude and frequency as noted previously) to uniformly distribute any leached colorant. Use a 5 ml disposable syringe to extract approximately 3-4 ml of liquid from the sample jar. Place a syringe filter (glass fiber, 1 micrometer pore size) on the syringe and filter the liquid mto a 1 cm pathlength spectrophotometer cuvette

Measure the absorbance of the sample at a wavelength of 616 nm usmg a properly calibrated visible or UV-visible spectrophotometer The spectrophotometer is calibrated by imtially preparmg a set of standards made by dissolving the acid form of bromocresol green mto the synthetic urme described above The standards should be made in the following concentrations by first weighing out exactly 0 100 g of the acid form of bromocresol green on an analytical balance accurate to three decimal places and dissolving the mdicator in 2999 9 g of synthetic urine at room temperature to produce the most concentrated sample and then diluting the most concentrated sample by weight to produce the less concentrated samples The standard concentrations are noted below

TABLE 2 Composition of Colorant Standards for Instrument Calibration

A synthetic urme blank should also be included in the set of standards Zero the absorbance of the spectrophotometer at 616 nm usmg the synthetic urme blank Measure and record the absorbance for each of the bromocresol green standards and the synthetic urme blank Plot the absorbance versus concentration and calculate the best fitting equation to the plotted data Use this fitted calibration curve equation to calculate the concentration of the bromocresol green in the unknown diffusion samples

From the calculated colorant concentration m each unknown, calculate the actual micrograms of colorant leached from the wetness mdicator sample mto the 20 0 g of synthetic urme at each time interval Divide this calculated amount of colorant leached mto the synthetic urme by the total gram weight of wetaess mdicator imtially coated onto the blank diaper backsheet disk Report and record this result as the Leachmg Value m units of micrograms of colorant leached per gram of wetness mdicator The 20 Minute Leaching Value is defined as the micrograms of colorant leached per gram of wetaess mdicator during exposure to 20 0 grams of synthetic urme for 20 minutes

1 Hour Leaching Value Test Method

The 1 Hour Leachmg Value Test Method is identical to the 20 Mmute Leaching Value Test Method except the prepared samples are exposed to 20 0 grams of the synthetic urine for a total time of 1 hour rather than 20 minutes The 1 Hour Leaching Value is defined as the micrograms of colorant leached per gram of wetaess mdicator during exposure to 200 grams of synthetic urine for 1 hour 3 Horn Leaching Value Test Method

The 3 Hour Leachmg Value Test Method is identical to the 20 Mmute Leachmg Value Test Method except the prepared samples are exposed to 20 0 grams of the synthetic urme for a total time of 3 hours rather than 20 mmutes The 3 Hour Leachmg Value is defmed as the micrograms of colorant leached per gram of wetaess indicator during exposure to 20 0 grams of synthetic urme for 3 hours

14 Hour Leaching Value Test Method

The 14 Hour Leachmg Value Test Method is identical to the 20 Mmute Leachmg Value Test Method except the prepared samples are exposed to 20 0 grams of the synthetic urme for a total time of 14 hours rather than 20 mmutes The 14 Hour Leachmg Value is defined as the micrograms of colorant leached per gram of wetaess indicator durmg exposure to 20 0 grams of synthetic urine for 14 hours

The following Table 3 summarizes the Leachmg Values measured at the four exposure times of 20 minutes, 1 hour, 3 hours, and 14 hours for three formulas that are examples of compositions of this mvention and one commercially available hot melt wetness mdication (HMWI) composition available from Bostik-Findley, Milwaukee, WI, U S A This commercially available HMWI is designated HMWI-1 Leachmg Values for all four of the compositions listed m table 1 were measured by usmg the previously descnbed Leachmg Value Test Methods, thus, the samples within the row designation of 0 33 hrs were tested usmg the 20 Mmute Leachmg Value Test Method The samples within the row designation of 1 00 hrs were tested usmg the 1 hour Leachmg Value Test Method and so on The means listed m columnar form for each composition were the anthmetic mean Leachmg Values as calculated from eight replicates for each unique composition at each unique exposure time Thus for example, the mean calculated for Formula 3 at 3 hours denotes a mean 3 Hour Leachmg Value of 250 micrograms of pH indicator per gram of wetaess indicator as calculated by taking the average of eight replicates

The compositions designated in Table 3 as Formula 1, Formula 2, and Formula 3 were made according to the directions given below It is clear from the tabulated results that the quaternary ammonium salt containing compositions of Formula 1 and Formula 2 are superior to both Formula 3 and the HMWI-1 m inhibiting leaching of the pH indicator (bromocresol green) at all synthetic urine exposure times As noted previously, this is hypothesized to be due to the ionic chemical bond formed between the cationic quaternary ammonium salt and the activated aniomc pH indicator This coacervate inhibits leachmg of the pH indicator due to its low solubility in the aqueous synthetic mine and its high solubility in the carrier matrix due to intermolecular bindmg forces

It is also important to note that even though the non-quaternary contammg Formula 3 listed below was mfenor to the quaternary contammg Formula 1 and 2, it was superior to the hot melt wetaess indicator designated as HMWI-1 As noted, the inhibition of leachmg m Formula 3 is due to intermolecular binding forces between the colorant and other components of the earner matrix Specifically for Formula 3, the wax, stearyl alcohol, C20-C40 Pareth-40, and the stearyl phosphate could also participate in intermolecular binding with the activated bromocresol green pH mdicator TABLE 3

Figure 6 shows a graph with the Leaching Values as measured by the previously described procedures for four synthetic urine exposure times: 20 minutes, 1 hour, 3 hours, and 14 hours. The y-axis denotes the micrograms of pH indicator leached per gram of wetaess indicator while the x-axis denotes the exposure time. The graph clearly shows the superiority of the catiomc quaternary ammonium compound containing formulas 1 and 2 in inhibiting leaching of the colorant. In this case, the colorant is activated bromocresol green and the leaching inhibitor is a cationic quaternary ammonium salt. The superior leaching inhibition is due to the previously described coacervate formation and binding of this coacervate within the carrier matrix due to the previously described intermolecular forces. The detailed composition and recipe information is given below for each of the formulas 1 through 3. As noted, the non-quaternary containing formula 3 below also inhibits leaching more effectively than the HMWI (designated HMWI-1). This is due to the previously described intermolecular binding forces present in this Formula 3. The amount of leaching in each of these compositions was measured by using the Leaching Value Test Methods described previously. The bar 90 denoted in Figure 6 notes the preferred 20 Minute Leaching Value of less than 300 micrograms of colorant leached per gram of wetaess indicator and bar 92 denotes the most preferred 20 Minute Leaching Value of less than 100 micrograms of colorant leached per gram of wetaess indicator as measured via the 20 Minute Leaching Value Test Method described previously. Bar 94 denotes the preferred 3 Hour Leaching Value of less than 600 micrograms of colorant leached per gram of wetness indicator, bar 96 denotes the more preferred 3 Hour Leaching Value of less than 300 micrograms of colorant leached per gram of wetaess indicator, and bar 98 denotes the most preferred 3 Horn Leaching Value of less than 100 micrograms of colorant leached per gram of wetaess indicator. All of the 3 Hour Leaching Values were measure using the 3 Horn Leaching Value Test Method as described previously.

Figure 7 shows a bar graph with the Leaching Values as measured by the previously described Leaching Value Test Methods for four synthetic urine exposure times: 20 minutes, 1 hour, 3 hours, and 14 hours. The y-axis denotes the micrograms of pH indicator leached per gram of wetness indicator while the x-axis denotes the exposure time. The bar graph once again clearly shows the superiority of the cationic quaternary ammonium containing formulas 1 and 2 in inhibiting leaching of the colorant. In this case, the colorant is activated bromocresol green and the leaching inhibitor is a quaternary ammonium salt. The superior leaching inhibition is due to the previously described coacervate formation and binding of this coacervate within the carrier matrix due to the previously described intermolecular forces. The detailed composition and recipe information is given below for each of the formulas 1 through 3. As noted, the non- quaternary contammg formula 3 also inhibits leaching more effectively than the HMWI (designated HMWI- 1) This is due to the previously described intermolecular binding forces present m this Formula 3 The amount of leachmg m each of these compositions was measured by usmg the Leaching Value Test Methods described previously The bar 90 denoted m Figure 7 notes the preferred 20 Mmute Leachmg Value of less than 300 micrograms of colorant leached per gram of wetaess and bar 92 denotes the most preferred 20 Mmute Leaching Value of less than 100 micrograms of colorant leached per gram of wetaess indicator as measured via the 20 Minute Leachmg Value Test Method described previously Bar 94 notes the preferred 3 Horn Leaching Value of less than 600 micrograms of colorant leached per gram of wetaess mdicator, bar 96 notes the more preferred 3 Hour Leachmg Value of less than 300 micrograms of colorant leached per gram of wetness mdicator, and bar 98 notes the most preferred 3 Hour Leachmg Value of less than 100 micrograms of colorant leached per gram of wetaess indicator All of the 3 Hour Leaching Values were measure usmg the 3 Horn Leachmg Value Test Method as described previously

Exemplary Embodiments

The unique blends havmg the following compositions exemplify the mvention The numbers for each formula are identical to the formula numbers described previously

FORMULA 1

Function Class Chemical Name Weight Percent

Carrier Matnx Fatty Alcohol Stearyl Alcohol

49 8%

Carrier Matnx Wax Microcrystalline Wax

10 0%

Acid Orgamc Acid Stearyl Phoshate (acid form)

10 0%

Leaching Inhibitor Quaternary Dιmethyl(2-ethylhexylhydrogenated

Ammonium compound tallowalkyl)ammonιum methyl sulfate 10 0%

Colorant pH Indicator Bromocresol Green (acid form)

0 2%

Surfactant Nomonic Type C20-C40 Pareth-40

20 0%

The preceding Formula 1 is made by first weighing out the correct amounts of stearyl alcohol, microcrystallme wax, and stearyl phosphate mto a stamless steel container The stearyl alcohol should be a white waxy solid with a punty of at least 97% and such a stearyl alcohol may have no more than 2% of arachidyl alcohol, and may possess a melt pomt of 56-60°C The product designated C01897 stearyl alcohol available from The Procter & Gamble Company of Cmcmnati, OH, U S A is a current example of an acceptable material. The microcrystalline wax should be a high molecular weight petroleum based wax consisting of saturated branched and cyclic non-polar hydrocarbons and such a wax may have a melting point in the range of 60-95°C. The product designated MULTIWAX™ W-835 available from the Crompton Corporation of Petrolia, PA, U.S.A. is a good example of a microcrystalline wax meeting these requirements. Arlatone™ MAP 180 is a good example of stearyl phosphate as available from Uniqema Incorporated in Wilmington, DE, U.S.A. Heat and mix this mixture at 100-110°C until this mixtare is clear, transparent and colorless. Add the correct amount of the dimethyl(2-ethylhexylhydrogenated tallowalkyl)ammonium methyl sulfate to the stearyl alcohol premix and heat at 100-110°C for 10 minutes. The dimethyl(2-ethylhexylhydrogenated tallowalkyl)ammonium methyl sulfate may have a quaternary salt content of 81.5-84.5%, may possess a free amine and free amine salt impurity content of no more than 4%, and may possess an HLB of 17-18. The product designated ARQUAD™ HTL8(W)-MS available from Akzo-Nobel of Chicago, IL, U.S.A. is a good example of a dialkyldimethyl quaternary ammonium salt currently meeting these requirements. To this mixture, add the correct amount of the powdered acid form of bromocresol green (as available from the Aldrich Chemical Company, Milwaukee, WI, U.S.A.). Heat and mix at 100-110°C for 20 mixtures. Finally, to this mixture, add the correct amount of C20-C40 Pareth-40 which has been preheated to a temperature of 110-110°C. Such a C20-C40 Pareth-40 may have a molecular weight (M_n) between 2200 and 2400, an ethylene oxide content between 75-85%, an HLB of approximately 16, and a melting point between 80-94°C. The product designated PERFORMATHOX™ 480 available from New Phase Technologies of Sugar Land, TX, U.S.A is a good example of a C20-C40 Pareth-40 meeting these requirements. Mix the entire composition at 100-110°C until it is clear, transparent and yellow-orange in color. Dispense into appropriate containers and allow to cool to room temperature.

FORMULA 2: Function Class Chemical Name Weight Percent

Carrier Matrix Fatty Alcohol Stearyl Alcohol

41.78% Carrier Matrix Wax Microcrystalline Wax

8.42% Surfactant Nonionic Type C20-C40 Pareth-40

19.64% Acid Organic Acid Stearyl Phoshate (acid form)

9.82% Colorant pH Indicator Bromocresol Green (acid form)

0.20% Leaching Inhibitor Quaternary Ammonium Dimethyl(2-ethylhexylhydrogenated compound tallowalkyl)ammonium methyl sulfate 10.12% Viscosity Increasing Modified Clay Quaternium-18 Hectorite

10.02% Agent

The preceding Formula 2 is made by first weighing out the correct amounts of stearyl alcohol, microcrystalline wax, dimethyl(2-ethylhexylhydrogenated tallowalkyl)ammonium methyl sulfate, and quaternium-18 hectorite. The stearyl alcohol should be a white waxy solid with a purity of at least 97% and such a stearyl alcohol may have no more than 2% of arachidyl alcohol, and may possess a melt point of 56- 60°C. The product designated CO 1897 stearyl alcohol available from The Procter & Gamble Company of Cincinnati, OH, U.S.A. is a current example of an acceptable material. The microcrystalline wax should be a high molecular weight petroleum based wax consisting of saturated branched and cyclic non-polar hydrocarbons and such a wax may have a melting point in the range of 60-95 °C. The product designated MULTIWAX™ W-835 available from the Crompton Corporation of Petrolia, PA, U.S.A. is a good example of a microcrystalline wax meeting these requirements. The dimethyl(2-ethylhexylhydrogenated tallowalkyl)ammonium methyl sulfate may have a quaternary ammonium salt content of 81.5-84.5%, may possess a free amine and free amine salt impurity content of no more than 4%, and may possess an HLB of 17-18. The product designated ARQUAD™ HTL8(W)-MS available from Akzo-Nobel of Chicago, IL, U.S.A. is a good example of a dialkyldimethyl quaternary ammonium salt currently meeting these requirements. BENTONE GEL™ MIO is a good example of quaternium-18 hectorite as available from Rheox Incorporated, Hightstown, NJ, U.S.A.. Heat this mixture to 90°C and mix with a prop mixer for 15 minutes. Next, shear this mixture with a laboratory shear mixer set to 16,000 RPM for 15 minutes. In a separate container, weigh out the correct amounts of C20-C40 Pareth-40, the acid form of stearyl phoshate, and the acid form of bromocresol green (as available from the Aldrich Chemical Company, Milwaukee, WI, U.S.A.) and heat and mix at 100°C until this second mixture is clear, transparent and orange in color. Such a C20-C40 Pareth-40 may have a molecular weight (M_n) between 2200 and 2400, an ethylene oxide content between 75-85%, an HLB of approximately 16, and a melting point between 80-94°C. The product designated PERFORMATHOX™ 480 available from the Crompton Corporation of Petrolia, PA, U.S.A. is a good example of a C20-C40 Pareth-40 meeting these requirements. Arlatone™ MAP 180 is a good example of stearyl phosphate as available from Uniqema Incorporated in Wilmington, DE, U.S.A.. After shearing the first mixture, add the correct amount of the heated (90-100°C) second mixture and prop mix for 15 minutes until the entire composition is opaque, homogeneous, and orange in color. Dispense into appropriate containers and allow to cool to room temperature.

FORMULA 3: Function Class Chemical Name Weight

Percent Carrier Matrix Fatty Alcohol Stearyl Alcohol

39.60% Carrier Matrix Wax Microcrystalline Wax

39.60% Surfactant Nonionic Type C20-C40 Pareth-40

20.0% Acid Organic Acid Stearyl Phoshate (acid form)

0.60% Colorant pH Indicator Bromocresol Green (acid form)

0.20%

The preceding Formula 3 is made by first weighing out the correct amounts of stearyl alcohol, and microcrystalline wax into a stainless steel container. The stearyl alcohol should be a white waxy solid with a purity of at least 97% and such a stearyl alcohol may have no more than 2% of arachidyl alcohol, and may possess a melt point of 56-60°C. The product designated C01897 stearyl alcohol available from The Procter & Gamble Company of Cincinnati, OH, U.S.A. is a current example of an acceptable material. The microcrystalline wax should be a high molecular weight petroleum based wax consisting of saturated branched and cyclic non-polar hydrocarbons and such a wax may have a melting point in the range of 60- 95°C. The product designated MULTIWAX™ W-835 available from the Crompton Corporation of Petrolia, PA, U.S.A. is a good example of a microcrystalline wax meeting these requirements. Heat and mix at 90-100°C until this mixture of stearyl alcohol and microcrystalline wax is clear, transparent and colorless. In a separate container, weigh out the correct amounts of C20-C40 pareth-40, the acid form of stearyl phoshate, and the acid form of bromocresol green (as available from the Aldrich Chemical Company, Milwaukee, WI, U.S.A.). Arlatone™ MAP 180 is a good example of stearyl phosphate as available from Uniqema Incorporated m Wilmington, DE, U S A. Such a C20-C40 Pareth-40 may have a molecular weight (M_n) between 2200 and 2400, an ethylene oxide content between 75-85%, an HLB of approximately 16, and a meltmg pomt between 80-94°C. The product designated PERFORMATHOX™ 480 as available from New Phase Technologies of Sugar Land, TX, U.S A is a good example of a C20-C40 Pareth-40 meeting these requirements Heat this second mixture to a temperature of 100-110°C and mix until it is clear, transparent and orange m color Next, slowly add the contents of this second mixture to first mixture contammg the stearyl alcohol and microcrystallme wax. Heat to 90-100°C and mix until the entire mixture is clear, transparent and orange m color. Dispense into appropriate containers and allow to cool to room temperature.

The wetaess mdicator may be applied to a substrate via any means of liquid or semi-liquid application as known m the art, including, but not limited to, slot coating, spraymg, gravure printing, ink jet pnntmg, and digital printing Alternatively, the wetaess mdicator may be a solid or semi-solid material affixed to a substrate via adhesive bonding, chemical bondmg or intermolecular force bonding Multiple mdicators may be applied to the same substrate m overlapping or nonoverlapping geometries The solidification process may be accelerated via the use of convective mass transport, if evaporation of a solvent is required, or convective or conductive heat transfer, e.g , coolmg via air or chilled rolls, etc.

The substrate to which the wetaess mdicator is applied or otherwise affixed may comprise any one, or a combmation, of the structural components of the article, mcludmg the backsheet, topsheet, fasteners, absorbent material, etc., or may be a separate element added or applied to the product The substrate may be a film, nonwoven, woven, or foam material and may comprise synthetic and/or natural materials

The indicator preferably provides a signal visible from outside the product while the product is being worn. Preferably, the signal, I e , color or contrast change, is visible through the backsheet or garment-facing covermg of the article. The signal preferably is visible within a short time after urmation Generally, the signal should be visible within about 15 mmutes after urme contacts the indicator. Preferably, the signal is visible within about 5 minutes after contact with urine In certain embodiments, the absorbent system of the article may be designed to allow urine to contact the mdicator in certain regions of the product at various loadmg levels. For example, the absorbent system may be designed to allow urme to contact the wetaess indicator in the crotch region of the product on the first urmation, but contact the wetaess indicator m other regions of the product only after the amount of urme m the product reaches a predetermined threshold value. For example, the absorbent core may have limited ability to distribute urine from a given region of the article until it contains sufficient urme to activate a wetaess indicator in this region, thereby preventing activation of the wetaess mdicator m adjacent regions of the article until the overall urine loadmg m the article increases above a given level. As the total urme loadmg m the article increases, more regions of the articles will contam sufficient urme to activate wetaess mdicators that may be located m those regions.

The wetness indicator may comprise two or more colorants, each having different activating criteria, I e , different pK_a values, a pH and an enzyme trigger, etc , colors, or other properties The wetness indicating compositions may be applied in any pattern or in conjunction with permanent graphics on the outer surfaces of a wearable article, as disclosed in US Patent 4,022,211 issued to Timmons, which is herein incorporated by reference. The varying colors, triggers, etc., may facilitate interactive scenes, sequences, or displays providing information regarding relative fullness/wetness of the article or merely provide entertainment and/or aesthetic value. For example, the wetness indicating composition may contain one colorant that turns blue and another that turns red upon contact with urine. Alternatively, one portion of the graphic may appear and another portion may disappear upon contact with urine.

The wetaess indicating compositions of the present invention may be adapted to detect the presence of residual feces on the skin of a wearer. The pH of feces typically ranges from about pH 5 to about pH 8. Once exposed to the air, fecal pH increases by about 0.5 pH unit every 30 minutes. Thus, compositions having pH transition values of about 7-8 may reliably detect the presence of residual fecal contamination at least about 1-2 hours old. Incorporation of these fecal contamination- indicating compositions onto a wearer-contacting surface, such as the topsheet, of a wearable article facilitates the transfer of the composition to the wearer's skin. The presence of fecal contamination, i.e., high pH material, on the skin causes the colorant to activate and display a signal to the caregiver indicating the need for additional or more through cleaning of the skin, particularly in the area where the presence of residual fecal material is indicated. The advantage of this embodiment is the resultant reduced possibility of the colorant penetrating the wearer's skin versus the application/transfer of the colorant alone to the skin. Penetration of the colorant in this example is inhibited due to the binding of the colorant to components of the wetness indicating composition that are too large to effectively diffuse into the skin.

Claims

1. A wetness indicating composition comprising a colorant disposed in a canier matrix, the carrier matrix comprising a leaching inhibitor, the colorant providing a visible signal when activated by urine and resisting leaching from the carrier matrix by being chemically or intermolecularly bound to the leaching inhibitor.

2. The wetaess indicating composition of Claim 1 wherein the colorant is a pH indicator.

3. The wetaess indicating composition of Claim lor 2 wherein the leaching inhibitor comprises a cationic species.

4. The wetness indicating composition of Claim 1 or 2 wherein the carrier matrix comprises a microcrystalline wax.

5. The wetaess indicating composition of Claim 1 or 2 wherein the carrier matrix comprises a surfactant.

6. The wetaess indicating composition of Claim 1 or 2 wherein the colorant is ionically or covalently bound to the leaching inhibitor.

7. The wetaess indicating composition of Claim 1 or 2 wherein the canier matrix comprises a C12-C50 linear primary alcohol.

8. The wetness indicating composition of Claim 1 or 2 wherein the canier matrix comprises an organic acid.

9. The wetaess indicating composition of any of the preceding claims wherein the canier matrix comprises a viscosity increasing agent.

10. The wetness indicating composition of any of the preceding claims having a colorant Leaching Value of no more than 300 micrograms of colorant leached per gram of the wetness indicator as measured by the herein disclosed 3 Hour Leaching Value Test Method.