WO2003072658A1 - Kaolin clay pigment for paper coating and method for producing same - Google Patents
Kaolin clay pigment for paper coating and method for producing same Download PDFInfo
- Publication number
- WO2003072658A1 WO2003072658A1 PCT/US2002/040926 US0240926W WO03072658A1 WO 2003072658 A1 WO2003072658 A1 WO 2003072658A1 US 0240926 W US0240926 W US 0240926W WO 03072658 A1 WO03072658 A1 WO 03072658A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pigment
- paper
- kaolin
- coated
- brightness
- Prior art date
Abstract
Description
Claims