WO2003089502A1 - Coating composition containing an epoxide additive and structures coated therewith - Google Patents
Coating composition containing an epoxide additive and structures coated therewith Download PDFInfo
- Publication number
- WO2003089502A1 WO2003089502A1 PCT/US2003/010672 US0310672W WO03089502A1 WO 2003089502 A1 WO2003089502 A1 WO 2003089502A1 US 0310672 W US0310672 W US 0310672W WO 03089502 A1 WO03089502 A1 WO 03089502A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- top coat
- coated
- coating
- layer
- gas
- Prior art date
Abstract
Description
Claims