WO2003089508A1 - Novel boehmite particles and polymer materials incorporating same - Google Patents
Novel boehmite particles and polymer materials incorporating same Download PDFInfo
- Publication number
- WO2003089508A1 WO2003089508A1 PCT/US2003/011941 US0311941W WO03089508A1 WO 2003089508 A1 WO2003089508 A1 WO 2003089508A1 US 0311941 W US0311941 W US 0311941W WO 03089508 A1 WO03089508 A1 WO 03089508A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- boehmite particles
- boehmite
- polymer
- particles
- polymer base
- Prior art date
Abstract
Description
Claims