WO2004009693A1 - Low polarity dimerate and trimerate esters as plasticizers for elastomers - Google Patents
Low polarity dimerate and trimerate esters as plasticizers for elastomers Download PDFInfo
- Publication number
- WO2004009693A1 WO2004009693A1 PCT/US2003/021866 US0321866W WO2004009693A1 WO 2004009693 A1 WO2004009693 A1 WO 2004009693A1 US 0321866 W US0321866 W US 0321866W WO 2004009693 A1 WO2004009693 A1 WO 2004009693A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- branched
- composition
- carbon
- straight chain
- alcohol
- Prior art date
Abstract
Description
Claims