WO2004044319A2 - Low slough tissue products and method for making same - Google Patents
Low slough tissue products and method for making same Download PDFInfo
- Publication number
- WO2004044319A2 WO2004044319A2 PCT/US2003/033634 US0333634W WO2004044319A2 WO 2004044319 A2 WO2004044319 A2 WO 2004044319A2 US 0333634 W US0333634 W US 0333634W WO 2004044319 A2 WO2004044319 A2 WO 2004044319A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- synthetic
- polymer
- tissue sheet
- tissue
- mixtures
- Prior art date
Abstract
Description
Claims