WO2004061232A1 - Process for bonding chemical additives on to substrates containing cellulosic materials and products thereof - Google Patents
Process for bonding chemical additives on to substrates containing cellulosic materials and products thereof Download PDFInfo
- Publication number
- WO2004061232A1 WO2004061232A1 PCT/US2003/032228 US0332228W WO2004061232A1 WO 2004061232 A1 WO2004061232 A1 WO 2004061232A1 US 0332228 W US0332228 W US 0332228W WO 2004061232 A1 WO2004061232 A1 WO 2004061232A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- moiety
- amino
- chemical additive
- article
- amine
- Prior art date
Abstract
Description
Claims