WO2005024131A1 - Method for applying an application medium containing starch onto a web of fibrous material - Google Patents

Method for applying an application medium containing starch onto a web of fibrous material Download PDF

Info

Publication number
WO2005024131A1
WO2005024131A1 PCT/EP2004/051911 EP2004051911W WO2005024131A1 WO 2005024131 A1 WO2005024131 A1 WO 2005024131A1 EP 2004051911 W EP2004051911 W EP 2004051911W WO 2005024131 A1 WO2005024131 A1 WO 2005024131A1
Authority
WO
WIPO (PCT)
Prior art keywords
starch
application medium
fibrous web
web
applying
Prior art date
Application number
PCT/EP2004/051911
Other languages
German (de)
French (fr)
Inventor
Robert Kling
Original Assignee
Voith Paper Patent Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Voith Paper Patent Gmbh filed Critical Voith Paper Patent Gmbh
Publication of WO2005024131A1 publication Critical patent/WO2005024131A1/en

Abstract

The invention relates to a method for applying an application medium (3, 7) containing starch onto a web of fibrous material (4,8) in the pressing section (1) and/or in the sieving section (5) of a machine in the production of paper, cardboard or tissue. The invention is characterised in that the application medium (3, 7) containing starch penetrates the fibrous material (4, 8) in an improved manner and with a determined concentration of starch.

Description

Verfahren zum Aufbringen eines stärkehaltigen Auftragsmediums auf eine Faserstoffbahn Process for applying a starchy application medium to a fibrous web
Die Erfindung betrifft ein Verfahren zum Aufbringen eines stärkehaltigen Auftragsmediums auf eine Faserstoffbahn in der Pressen- und/oder in der Siebpartie einer Maschine zur Herstellung von Papier, Karton oder Tissue.The invention relates to a method for applying a starch-containing application medium to a fibrous web in the press and / or in the wire section of a machine for the production of paper, cardboard or tissue.
Nach dem Stand der Technik werden bei der Papier-, Karton-, oder Tissue- herstellung stärkehaltige Auftragsmedien in der Sieb- und/oder in der Pressenpartie einer Papiermaschine auf Faserstoffbahnen aufgebracht, wodurch Eigenschaften der Faserstoffbahn, wie beispielsweise die Festigkeit, die Wasseraufnahme und die Bedruckbarkeit beeinflusst werden.According to the prior art, starch-containing application media are applied in the wire and / or in the press section of a paper machine to fibrous webs in the manufacture of paper, cardboard or tissue, whereby properties of the fibrous web, such as for example the strength, the water absorption and the Printability can be influenced.
Die Auftragsmedien, die bei den aus dem Stand der Technik bekannten Verfahren verwendet werden, enthalten hierbei native oder modifizierte Stärken. Bei der Verwendung von Auftragsmedien mit nativer oder modifizierter Stärke sind bezüglich der Menge des Auftragsmediums, die auf eine Faserstoffbahn aufbringbar ist, bezüglich des Eindringens des Auftragsmediums in die Faserstoffbahn sowie be- züglich der Dosierung der dem Auftragsmedium zugesetzten Stärke Grenzen gesetzt. Dies hat zur Folge, dass auch die Eigenschaften der Faserstoffbahn nur innerhalb dieser Grenzen beeinflusst werden können. Nach dem Stand der Technik werden in der Pressenpartie modifizierte Stärken eingesetzt. Die Aufbringung des stärkehaltigen Auftragsmediums auf die Faserstoffbahn erfolgt über eine Spritzeinrichtung (Spritzrohr, Sprührohr). Um einen maximalen Festigkeitsanstieg zu erreichen, ist man bestrebt, eine möglichst große Menge an Stärke auf die Faserstoffbahn aufzubringen.The application media used in the processes known from the prior art contain native or modified starches. When using application media with native or modified starch, there are limits to the amount of application medium that can be applied to a fibrous web, the penetration of the application medium into the fibrous web and the dosage of the starch added to the application medium. As a result, the properties of the fibrous web can only be influenced within these limits. According to the state of the art, modified starches are used in the press section. The starch-containing application medium is applied to the fibrous web via a spray device (spray tube, spray tube). In order to achieve a maximum increase in strength, the aim is to apply the greatest possible amount of starch to the fibrous web.
Das kann prinzipiell dadurch erreicht werden, indem bei einer gegebenen Konzentration der Stärke im Auftragsmedium die Menge des Auftragsmediums, die auf die Faserstoffbahn aufgebracht wird, erhöht wird. Die Menge des stärkehal- tigen Auftragsmediums, die auf die Faserstoffbahn aufgebracht werden kann, ist dadurch limitiert, dass der Trockengehalt der Faserstoffbahn bei hohen Mengen an aufgebrachtem Auftragsmedium zu stark abfällt, was zu einer Verringerung der Reißfestigkeit der Faserstoffbahn und zu deren Abriss führen kann. Darüber hinaus wird die Energie zum Trocknen einer Faserstoffbahn stark von der Menge des aufgebrachten Auftragsmediums beeinflusst.In principle, this can be achieved by increasing the amount of application medium that is applied to the fibrous web at a given concentration of starch in the application medium. The amount of starch-containing application medium that can be applied to the fibrous web is limited by the fact that the dry content of the fibrous web drops too much with high amounts of applied application medium, which can lead to a reduction in the tear strength of the fibrous web and to its tearing. In addition, the energy for drying a fibrous web is strongly influenced by the amount of application medium applied.
Eine weitere Möglichkeit, die Menge der Stärke, die auf die Faserstoffbahn aufgebracht wird, zu maximieren, ist, die Konzentration der Stärke im Auftragsmedium zu erhöhen. Die Konzentration der Stärke im Auftragsmedium ist begrenzt, weil mit zunehmender Konzentration der Stärke im Auftragsmedium die Viskosität des Auftragsmediums zunimmt (typische Werte sind 20 bis 25 mPa.s bei einer Konzentration von 8 % und 40 bis 50 mPa.s bei einer Konzentration von 11 % der modifizierten Stärke im Auftragsmedium). Das führt bei hohen Konzentrationen der Stärke im Auftragsmedium zu Problemen beim Aufbringen des Auftragsme- diums durch Sprühen und zu einem schlechteren Eindringen (Penetration) des Auftragsmediums in die Faserstoffbahn. Ein gutes Eindringen des Auftragsmediums in die Faserstoffbahn ist jedoch Voraussetzung für die gewünschte Zunahme der Festigkeiten der Faserstoffbahn.Another way to maximize the amount of starch that is applied to the fibrous web is to increase the concentration of the starch in the application medium. The concentration of the starch in the application medium is limited because the viscosity of the application medium increases with increasing concentration of the starch in the application medium (typical values are 20 to 25 mPa.s at a concentration of 8% and 40 to 50 mPa.s at a concentration of 11 % of the modified starch in the application medium). At high concentrations of the starch in the application medium, this leads to problems when applying the application medium by spraying and to poor penetration (penetration) of the application medium into the fibrous web. However, a good penetration of the application medium into the fibrous web is a prerequisite for the desired increase in the strength of the fibrous web.
Ein weiterer Nachteil besteht darin, dass das Auftragsmedium mit modifizierter Stärke klebrig ist und somit leicht zur Bildung von unerwünschten Ablagerungen führen kann. Nach dem Stand der Technik wird in der Siebpartie native Stärke eingesetzt. Die Aufbringung des stärkehaltigen Auftragsmediums auf die Faserstoffbahn erfolgt über eine Spritzeinrichtung (Spritzrohr, Sprührohr). Um einen maximalen Festig- keitsanstieg zu erreichen, ist man bestrebt, eine möglichst große Menge an Stärke auf die Faserstoffbahn aufzubringen. In der Siebpartie spielt die Konzentration der Stärke im Auftragsmedium keine Rolle, sondern einzig und allein die aufgebrachte Stärkemenge. Die Menge der Stärke ist dadurch begrenzt (zirka 1 ,5 % bezogen auf die gesamte Produktion), dass bei zu hohen Stärkemengen keine vollständige Verkleisterung der Stärke in der Trockenpartie stattfindet. Die Verkleisterung ist jedoch Voraussetzung für einen Festigkeitsanstieg.Another disadvantage is that the application medium with modified starch is sticky and can easily lead to the formation of undesirable deposits. According to the state of the art, native starch is used in the wire section. The starchy application medium is applied to the fibrous web via a spray device (spray tube, spray tube). In order to achieve a maximum increase in strength, the aim is to apply the greatest possible amount of starch to the fibrous web. In the wire section, the concentration of the starch in the application medium is irrelevant, but solely the amount of starch applied. The amount of starch is limited (approx. 1.5% based on the entire production) in that if the amount of starch is too high, there is no complete gelatinization of the starch in the dryer section. However, gelatinization is a prerequisite for an increase in strength.
Ein prinzipieller Nachteil des Einsatzes von nativer Stärke in der Siebpartie besteht in der schlechten Penetration der Stärke in die Faserstoffbahn, weil die na- tive Stärke in Form von Partikeln vorliegt (Kartoffelstärke: 80 % der Körner zwischen 7 und 70 Mikrometer, Maisstärke: 90 % der Körner zwischen 5 und 40 Mikrometer). Durch den Filtrationseffekt der Faserstoffbahn bleiben die Stärkepartikel an der Oberfläche der Faserstoffbahn, was zu einer ungleichmäßigen Verteilung der Stärke über die Dicke der Faserstoffbahn führt. Die ungleichmäßige Ver- teilung der Stärke über die Dicke der Faserstoffbahn wirkt sich nachteilig auf viele Festigkeitseigenschaften aus.A fundamental disadvantage of using native starch in the wire section is the poor penetration of the starch into the fibrous web, because the native starch is in the form of particles (potato starch: 80% of the grains between 7 and 70 micrometers, corn starch: 90% the grains between 5 and 40 microns). Due to the filtration effect of the fibrous web, the starch particles remain on the surface of the fibrous web, which leads to an uneven distribution of the starch over the thickness of the fibrous web. The uneven distribution of the starch over the thickness of the fibrous web has an adverse effect on many strength properties.
Ausgehend von den aus dem Stand der Technik bekannten Nachteilen besteht die Aufgabe der vorliegenden Erfindung darin, ein Verfahren zum Aufbringen eines stärkehaltigen Auftragsmediums vorzuschlagen, durch das es möglich ist, in weiterem Rahmen als bisher auf die Eigenschaften, insbesondere die Festigkeitseigenschaften, einer Faserstoffbahn einzuwirken.Based on the disadvantages known from the prior art, the object of the present invention is to propose a method for applying a starch-containing application medium, by means of which it is possible to act on the properties, in particular the strength properties, of a fibrous web in a wider scope than previously.
Gelöst wird diese Aufgabe durch ein Verfahren mit den Merkmalen des Patentan- spruchs 1.This object is achieved by a method with the features of patent claim 1.
Vorteilhafte Ausführungsformen und Weiterbildungen der Erfindung sind in den Unteransprüchen angegeben.Advantageous embodiments and developments of the invention are in the Subclaims specified.
Bei dem aus dem Stand der Technik bekannten Verfahren wird ein stärkehaltiges Auftragsmedium auf eine Faserstoffbahn in der Pressenpartie und/oder in der Siebpartie einer Maschine zur Herstellung oder Veredelung von Papier-, Karton-, oder Tissue aufgebracht.In the process known from the prior art, a starch-containing application medium is applied to a fibrous web in the press section and / or in the wire section of a machine for the production or finishing of paper, cardboard or tissue.
Beim erfindungsgemäßen Verfahren ist darüber hinaus vorgesehen, dass das verwendete stärkehaltige Auftragsmedium bei einer gegebenen Stärkekonzentra- tion eine verbesserte Penetration in die Faserstoffbahn aufweist, als ein stärkehaltiges Auftragsmedium mit nativer oder modifizierter Stärke. Eine hohe Penetration des stärkehaltigen Auftragsmediums in die Faserstoffbahπ ist Voraussetzung für die Erhöhung der Festigkeiten der Faserstoffbahn.In the method according to the invention it is further provided that the starch-containing application medium used has a better penetration into the fibrous web at a given starch concentration than a starch-containing application medium with native or modified starch. A high penetration of the starch-containing application medium into the fibrous web is a prerequisite for increasing the strength of the fibrous web.
Beim erfindungsgemäßeπ Verfahren sind für die Aufbringung der Stärke in der Pressenpartie Auftragsmedien vorgesehen, die eine niedrigere Viskosität besitzen als die nach dem Stand der Technik üblichen stärkehaltigen Auftragsmedien mit modifizierter Stärke. Bei den vorgeschlagenen stärkehaltigen Auftragsmedien handelt es sich im Wesentlichen um Suspensionen. Im Vergleich mit herkömm- liehen stärkehaltigen Auftragsmedien mit modifizierter Stärke besitzen diese bis zu hohen Konzentrationen (zum Beispiel 30 %) eine sehr niedrige Viskosität (typischer Wert < 30 mPa.s).In the process according to the invention, application media which have a lower viscosity than the starch-containing application media with modified starch customary in the prior art are provided for applying the starch in the press section. The proposed starchy application media are essentially suspensions. In comparison to conventional starch-containing application media with modified starch, these have a very low viscosity up to high concentrations (for example 30%) (typical value <30 mPa.s).
Daraus ergeben sich einige Vorteile. Wegen der niedrigeren Viskosität des stärke- haltigen Auftragsmediums sind höhere Konzentrationen verarbeitbar als mit herkömmlichen Auftragsmedien mit modifizierter Stärke.This has several advantages. Due to the lower viscosity of the starch-containing application medium, higher concentrations can be processed than with conventional application media with modified starch.
Durch den Einsatz eines Auftragsmediums mit einer höheren Stärkekonzentration wird der Trockengehalt der Faserstoffbahn beim Aufbringen einer bestimmten Stärkemenge auf die Faserstoffbahn weniger reduziert als bei einem aus dem Stand der Technik bekannten Verfahren unter Verwendung eines stärkehaltigen Auftragsmediums mit modifizierter Stärke. Das führt zu Vorteilen des erfindungs- gemäßen Verfahrens hinsichtlich Reißfestigkeit der Faserstoffbahn und der für die Trocknung notwendigen EnergieBy using an application medium with a higher starch concentration, the dry content of the fibrous web when applying a certain amount of starch to the fibrous web is reduced less than in a method known from the prior art using a starch-containing application medium with modified starch. This leads to advantages of the invention according to the procedure with regard to tensile strength of the fibrous web and the energy required for drying
Die niedrigere Viskosität des stärkehaltigen Auftragsmediums führt außerdem zu Vorteilen hinsichtlich Aufbringung des Auftragsmediums auf die Faserstoffbahn durch Sprühen und Penetration des Auftragsmediums in die Faserstoffbahn, was sich wiederum günstig auf die Festigkeitseigenschaften auswirkt.The lower viscosity of the starch-containing application medium also leads to advantages with regard to the application of the application medium to the fibrous web by spraying and penetration of the application medium into the fibrous web, which in turn has a favorable effect on the strength properties.
Wegen der geringeren Klebrigkeit der vorgeschlagenen stärkehaltigen Auftrags- medien sind außerdem geringere Probleme mit Ablagerungen zu erwarten.Because of the lower stickiness of the proposed starchy application media, fewer problems with deposits are to be expected.
Beim erfindungsgemäßen Verfahren sind für die Aufbringung der Stärke in der Siebpartie Auftragsmedien vorgesehen, die in die Faserstoffbahn besser eindringen als die nach dem Stand der Technik üblichen stärkehaltigen Auftragsmedien mit nativer Stärke. Es gibt verschiedene Gründe für die bessere Penetration des stärkehaltigen Auftragsmediums in die Faserstoffbahn. Fragmentierte und gemahlene Stärken dringen aufgrund der kleineren Partikel leichter in die Faserstoffbahn ein (90 % < 20 Mikrometer). Die Partikel der partikulär verkleisterten Stärken sind sogar größer als native Stärkekörner (typisch ist ein 20 bis 100 % größerer Durchmesser). Die bessere Penetration ist hier aufgrund der veränderten Oberfläche zu erklären. Durch die bessere Penetration ergeben sich Vorteile hinsichtlich der zu erreichenden Festigkeiten der Faserstoffbahn.In the process according to the invention, application media are provided for the application of the starch in the wire section, which penetrate the fibrous web better than the starch-containing application media with native starch which are customary in the prior art. There are various reasons for the better penetration of the starch-containing application medium into the fibrous web. Due to the smaller particles, fragmented and ground starches penetrate more easily into the fibrous web (90% <20 micrometers). The particles of the particulate gelatinized starches are even larger than native starch grains (a 20 to 100% larger diameter is typical). The better penetration can be explained here due to the changed surface. The better penetration results in advantages with regard to the strength of the fibrous web to be achieved.
Außerdem ist zu erwarten, dass mit diesen stärkehaltigen Auftragsmedien höhere Dosierungen als mit den üblichen stärkehaltigen Auftragsmedien mit nativer Stärke möglich sind , weil die Stärke dieser Auftragsmedien durch die vorangehenden Verarbeitungsschritte leichter verkleistert als native Stärke.In addition, it is to be expected that higher dosages will be possible with these starchy application media than with the usual starchy application media with native starch, because the starch of these application media pastes more easily than native starch due to the preceding processing steps.
Die nachfolgend beschriebenen stärkehaltigen Auftragsmedien besitzen erstens eine geringere Viskosität im Vergleich zu stärkehaltigen Auftragsmedien mit modifizierter Stärke (entscheidend für die Aufbringung in der Pressenpartie) und zweitens eine bessere Penetration in die Faserstoffbahn im Vergleich zu stärkehaltigen Auftragsmedien mit nativer Stärke (entscheidend für die Aufbringung in der Siebpartie).The starch-containing application media described below firstly have a lower viscosity compared to starch-containing application media with modified starch (crucial for application in the press section) and secondly a better penetration into the fibrous web compared to starchy material Application media with native strength (decisive for the application in the wire section).
Nach einer bevorzugten Ausführungsform der Erfindung ist die Stärke des ver- wendeten Auftragsmediums eine fragmentierte Stärke. Hierbei ist die fragmentierte Stärke dadurch herstellbar, indem in einem Verfahrensschritt ein Ausgangsstoff vorvernetzt wird, und indem in einem weiteren Verfahrensschritt das vorvernetzte Zwischenprodukt gemahlen wird. Als Ausgangsstoff kann native oder modifizierte Stärke Verwendung finden. Vorzugsweise wird der Ausgangsstoff mit Epichlorhydrin vorvernetzt.According to a preferred embodiment of the invention, the starch of the application medium used is a fragmented starch. Here, the fragmented starch can be produced by pre-crosslinking a starting material in one process step and by grinding the pre-crosslinked intermediate product in a further process step. Native or modified starch can be used as the starting material. The starting material is preferably pre-crosslinked with epichlorohydrin.
Eine weitere Möglichkeit zur Herstellung eines stärkehaltigen Auftragsmediums besteht in der Verwendung von partikulär verkleisterter Stärke. Diese wird durch die Zugabe einer definierten Menge Wasser zu einer Suspension von nativen Stärkekörnerπ in Butanol unter Erwärmen hergestellt.Another possibility for the production of a starch-containing application medium is the use of particulate gelatinized starch. This is produced by adding a defined amount of water to a suspension of native starch granules in butanol while heating.
Eine weitere Möglichkeit zur Herstellung eines stärkehaltigen Auftragsmediums besteht darin, native Stärke in Wasser zu mahlen.Another option for producing a starch-containing application medium is to grind native starch in water.
Des weiteren ist es denkbar, zur Herstellung eines stärkehaltigen Auftragsmediums native Stärke in organischen Lösungsmitteln zu mahlen.Furthermore, it is conceivable to grind native starch in organic solvents to produce a starch-containing application medium.
Da ein Teil der mit dem Auftragsmedium auf die Faserstoffbahn aufgebrachten Stärke bei dem nachfolgenden Entwässerungsschritt mit dem Wasser wieder aus- getragen wird, sieht eine bevorzugte Weiterentwicklung des erfindungsgemäßen Verfahrens vor, dass das mit ausgetragener Stärke versetzte Wasser in einem zu den übrigen Wasserkreisläufen separaten Wasserkreislauf geführt wird. Es sind verschiedene Möglichkeiten denkbar, das stärkehaltige Auftragsmedium auf die Faserstoffbahn aufzutragen. Eine Variante besteht darin, das stärkehaltige Auftragsmedium auf die Faserstoffbahn mittels Sprührohr (oder "Spritzrohr") aufzusprühen. Eine andere Möglichkeit ist, das stärkehaltige Auftragsmedium auf die Faserstoffbahn durch ein Walzenauftragsverfahren aufzutragen.Since part of the starch applied to the fibrous web with the application medium is discharged again with the water in the subsequent dewatering step, a preferred further development of the method according to the invention provides that the water mixed with starch is conducted in a water cycle separate from the other water cycles becomes. Various options are conceivable for applying the starch-containing application medium to the fibrous web. A variant consists in spraying the starchy application medium onto the fibrous web by means of a spray tube (or "spray tube"). Another possibility is to apply the starch-containing application medium to the fibrous web by means of a roller application process.
Nachfolgend wird die Erfindung anhand von schematischen Zeichnungen auf der Grundlage eines bevorzugten Ausführungsbeispiels näher erläutert. Es zeigen:The invention is explained in more detail below with the aid of schematic drawings based on a preferred exemplary embodiment. Show it:
Figur 1 eine Pressenpartie mit einem Sprührohr zur Durchführung des erfindungsgemäßen Verfahrens; Figur 2 eine Siebpartie mit einem Sprührohr zur Durchführung des erfindungsgemäßen Verfahrens.1 shows a press section with a spray tube for performing the method according to the invention; Figure 2 shows a wire section with a spray tube for performing the method according to the invention.
Die Figur 1 zeigt eine Pressenpartie 1 einer Papier-, Karton- oder Tissue- maschine. In der Pressenpartie 1 ist ein Sprührohr 2 zum Aufbringen eines stärkehaltigen Auftragsmediums 3 auf eine Faserstoffbahn 4 vorgesehen. FIG. 1 shows a press section 1 of a paper, cardboard or tissue machine. In the press section 1, a spray tube 2 is provided for applying a starch-containing application medium 3 to a fibrous web 4.
Die Figur 2 zeigt eine Siebpartie 5 einer Papier-, Karton- oder Tissuemaschine. In der Siebpartie 5 ist ein Sprührohr 6 zum Aufbringen eines stärkehaltigen Auftragsmediums 7 auf eine Faserstoffbahn 8 vorgesehen. FIG. 2 shows a wire section 5 of a paper, cardboard or tissue machine. In the wire section 5, a spray tube 6 is provided for applying a starch-containing application medium 7 to a fibrous web 8.
BezugszeichenlisteLIST OF REFERENCE NUMBERS
1 Pressenpartie1 press section
2, 6 Sprührohr2, 6 spray tube
3, 7 Stärkehaltiges Auftragsmedium3, 7 Starchy application medium
4, 8 Faserstoffbahn 5 Siebpartie 4, 8 fibrous web 5 wire section

Claims

Patentansprüche claims
1. Verfahren zum Aufbringen eines stärkehaltigen Auftragsmediums (3,7) auf eine Faserstoffbahn (4,8) in der Pressenpartie (1) und/oder in der Siebpartie (5) einer Maschine zur Herstellung einer Papier-, Karton- oder Tissuebahn, dadurch gekennzeichnet, dass das stärkehaltige Auftragsmedium (3,7) bei einer gegebenen Stärkekonzentration eine verbesserte Penetration in die Faserstoffbahn (4,8) aufweist.1. A method for applying a starch-containing application medium (3.7) to a fibrous web (4.8) in the press section (1) and / or in the wire section (5) of a machine for producing a paper, cardboard or tissue web, thereby characterized in that the starch-containing application medium (3,7) has a better penetration into the fibrous web (4,8) for a given starch concentration.
2. Verfahren nach Anspruch 1 , dadurch gekennzeichnet, dass die Stärke des Auftragsmediums (3,7) eine fragmentierte Stärke ist.2. The method according to claim 1, characterized in that the thickness of the application medium (3,7) is a fragmented thickness.
3. Verfahren nach Anspruch 2, dadurch gekennzeichnet, dass die fragmentierte Stärke dadurch hergestellt wird, dass in einem Verfahrensschritt native Stärke als Ausgangsstoff mit Epichlorhydrin vernetzt wird und dass in einem weiteren Verfahrensschritt das vernetzte Zwischenprodukt gemahlen wird.3. The method according to claim 2, characterized in that the fragmented starch is produced by crosslinking native starch as the starting material with epichlorohydrin in one process step and by grinding the crosslinked intermediate product in a further process step.
Verfahren nach Anspruch 1 , dadurch gekennzeichnet, dass die Stärke des Auftragsmediums (3,7) eine partikulär verkleisterte Stärke ist. A method according to claim 1, characterized in that the thickness of the application medium (3,7) is a particulate gelatinized starch.
5. Verfahren nach Anspruch 4, dadurch gekennzeichnet, dass der Grad der Verkleisterung der teilweise verkleisterten Stärke durch die Menge des zugegebenen Wassers eingestellt wird.5. The method according to claim 4, characterized in that the degree of gelatinization of the partially gelatinized starch is adjusted by the amount of water added.
6. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die Stärke des Auftragsmediums (3,7) eine in Wasser gemahlene Stärke ist.6. The method according to claim 1, characterized in that the starch of the application medium (3,7) is a starch ground in water.
7. Verfahren nach Anspruch 1 , dadurch gekennzeichnet, dass die Stärke des Auftragsmediums (3,7) eine in einem organischen Lö- sungsmittel gemahlene Stärke ist.7. The method according to claim 1, characterized in that the starch of the application medium (3,7) is a starch ground in an organic solvent.
8. Verfahren nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass das stärkehaltige Auftragsmedium (3,7) direkt mittels mindestens einer Spritzeinrichtung, insbesondere einer Vielzahl von Spritzrohren, oder indirekt mittels mindestes eines Walzenauftragswerks auf die Faserstoffbahn (4,8) aufgebracht wird.8. The method according to any one of the preceding claims, characterized in that the starch-containing application medium (3, 7) is applied directly to the fibrous web (4, 8) by means of at least one spray device, in particular a plurality of spray tubes, or indirectly by means of at least one roller application unit.
9. Verfahren nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass bei einem dem Aufbringen des stärkehaltigen Auftragsmediums (3,7) auf die Faserstoffbahn (4,8) nachfolgenden Entwässerungsschritt das mit ausgetragener Stärke versetzte Wasser in einem zu den übrigen Wasserkreisläufen separaten Wasserkreislauf geführt wird. 9. The method according to any one of the preceding claims, characterized in that when the starch-containing application medium (3.7) is applied to the fibrous web (4.8) following dewatering step, the starch-added water is conducted in a separate water circuit from the other water circuits becomes.
PCT/EP2004/051911 2003-09-03 2004-08-26 Method for applying an application medium containing starch onto a web of fibrous material WO2005024131A1 (en)