WO2005042427A2 - Method of forming microstructures on a substrate and a microstructured assembly used for same - Google Patents
Method of forming microstructures on a substrate and a microstructured assembly used for same Download PDFInfo
- Publication number
- WO2005042427A2 WO2005042427A2 PCT/US2004/033170 US2004033170W WO2005042427A2 WO 2005042427 A2 WO2005042427 A2 WO 2005042427A2 US 2004033170 W US2004033170 W US 2004033170W WO 2005042427 A2 WO2005042427 A2 WO 2005042427A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ribs
- mold
- substrate
- curable material
- rib
- Prior art date
Abstract
Description
Claims