WO2006066253A2

WO2006066253A2 - Antimicrobial water softener salt and solutions

Info

Publication number: WO2006066253A2
Application number: PCT/US2005/046150
Authority: WO
Inventors: Robert Scott Koefod
Original assignee: Cargill, Incorporated
Priority date: 2004-12-15
Filing date: 2005-12-15
Publication date: 2006-06-22
Also published as: CA2589517A1; WO2006066253A3; DE112005003140T5

Abstract

One embodiment of the present invention is a method of regenerating an ion exchange medium. Another embodiment of the invention is a system for the same comprising an antimicrobial agent reservoir (40) and a regenerating solution reservoir (30).

Description

ANTIMICROBIAL WATER SOFTENER SALT AND SOLUTIONS

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application claims the benefit of a) US Application No. 10/460,769, filed 12 June 2003 entitled ANTIMICROBIAL SALT SOLUTIONS FOR FOOD- SAFETY APPLICATIONS and b) US Provisional Application No. 60/636,337, filed 15 December 2004 entitled ANTIMICROBIAL WATER SOFTENER SALT AND SOLUTIONS and c) US Provisional Application No. 60/637,674, filed 16 December 2004 entitled ANTIMICROBIAL WATER SOFTENER SALT AND SOLUTIONS. The entirety of each of these applications is incorporated herein by reference.

BACKGROUND

[0002] This invention generally relates to salt-based formulations having antimicrobial activity and antimicrobial solutions made therefrom. Aspects of the invention have particular utility in connection with water softening and other applications in which ions in a solution may be removed or exchanged.

[0003] So-called "hard" water contains excess mineral salts, e.g., calcium and magnesium salts. A variety of techniques have been used to remove or replace ions of these mineral salts to "soften" the water. These techniques include distillation, adding water softening compounds to the water, membrane filtration, and ion exchange, e.g., cation exchange. Ion exchange-based water softening is used in a variety of industrial applications and is particularly prevalent in smaller-scale water softening systems used to treat water coming into individual homes. Ion exchange is also used to remove ions from water and other solutions in other applications.

[0004] Generally, ion exchange-based water treatment systems pass water through an ion exchange medium, which exchanges ions in the water with substitute ions, e.g., by exchanging mineral cations with cations of sodium or potassium. A wide variety of such media are known in the art, including resins, which may be strong or weak acid or strong or weak base ion exchange resins, and microporous minerals such as zeolites. For example, U.S. Patent Application Publication No. 2002/0072545 (published 13 June 2002, the entirety of which is incorporated herein by reference), suggests a synthetic ion exchange resin that may comprise a styrene-divinylbenzene copolymer or an acrylic-divinylbenzene copolymer. From time to time, such ion exchange media must be regenerated by exchanging preferred cations for the cations accumulated in the media from treating the hard water. This is typically accomplished by delivering brine to the ion exchange resin during a regeneration cycle that typically lasts on the order of 30 minutes. After passing through the ion exchange medium, the brine is commonly discharged into the environment.

[0005] Bacteria may become attached to the surface of the ion exchange medium and proliferate. Over time, the bacteria can create a biofilm on the medium, reducing efficacy of the medium. In some circumstances, the water exiting the ion exchange medium may have a bacteria population that is higher than the bacteria content of the water entering the ion exchange resin. Some opportunistic and disease-causing bacteria that have been found to flourish on ion exchange media may present health risks for the elderly and those with weakened immune systems if present in significant enough concentration. As a consequence, some European countries forbid the use of water softeners without a mechanism for disinfecting the water exiting the water softening system.

[0006] Reducing bacterial contamination of ion exchange media by delivering antimicrobial agents to the resin presents a number of difficulties. Calcium hypochlorite is inexpensive and is commonly recognized as a highly effective antimicrobial agent useful in a variety of applications. Unfortunately, calcium hypochlorite is known to reduce the useful life of many common ion exchange resins and manufacturers of such resins caution against its use. A variety of other common antimicrobial agents are ill-suited for applications in which they may be ingested, such as in softening potable water, because of health concerns and/or sensory degradation, e.g., adversely affecting the taste or odor of treated water. Adequately flushing the resin prior to reuse can ameliorate these effects, but consumers may still resist adopting approaches that employ chemicals they deem undesirable. Still other known antimicrobial agents are cost-prohibitive or present environmental waste disposal challenges. BRIEF DESCRIPTION OF THE DRAWING

[0007] Figure 1 is a schematic overview of a water softener system in accordance with an embodiment of the invention.

DETAILED DESCRIPTION

A. Overview

[0008] Salt has been used in water softener systems to rejuvenate ion exchange media. Acids and surfactants have been used as antibacterial agents in other applications. However, it has been discovered that inorganic salts act synergistically with acid and surfactant ingredients to provide a significant and unexpected increase in their antibacterial effectiveness. More particularly, initial tests revealed an unexpected, synergistic effect between sodium chloride and an acid/SLS (sodium lauryl sulfate) antimicrobial additive. Replicate tests were run to determine if this effect was significant. Solutions were also prepared containing an identical concentration of acid and SLS but no sodium chloride. Results of these tests, run with multiple replicates, illustrate that salt formulations including SLS and either citric acid or malic acid yield many fewer living microorganisms after 30 minutes than either plain NaCI or salt-free compositions of the same levels of SLS and citric or malic acid. Further testing suggests that the combination of at least select inorganic salts with surfactants can also yield surprising increases in the kill rates of bacteria when compared to either the salt alone or the surfactant alone.

[0009] Aspects of the invention described herein variously provide antimicrobial additives for a brine solution, salt-based formulations and solutions and water softener systems. One embodiment of the invention provides a mixture of a salt, such as sodium chloride, with an acid and a surfactant, such as sodium lauryl sulfate. Suitable acids include citric, malic, acetic, propionic, lactic, benzoic, ascorbic, isoascorbic, sorbic, phosphoric, hydrochloric, malic, tartaric, adipic, succinic, glutaric, salicylic, and sulfuric acids as well as sodium bisulfate. The salt can be selected from inorganic salts including the chloride, sulfate, nitrate, phosphate, carbonate, and hydroxide salts of sodium, potassium, magnesium, calcium, iron, and ammonium. Suitable surfactants include sodium lauryl sulfate, linear alkylbenzene sulfonates, alcohol sulfates, alpha-olefin sulfonates, alcohol ethoxylates, nonylphenyl ethoxylates, alkylpolyglucosides, fatty alkanoamides, fatty amine oxides, sodium dioctylsulfosuccinate, dodecylbenzene sulfonic acid and its salts, the sodium salt of sulfonated oleic acid, sodium dodecylbenzene sulfonate, and dodecyldiphenyloxide disulfonic acid and its salts.

[0010] As used herein, a "food-safe" substance, e.g., a "food-safe" surfactant, is a substance that is safe for human consumption at the levels anticipated to be present in water (for example) treated in accordance with embodiments of the invention. Although a "food-safe" substance may be classified by the US Food and Drug Administration as "generally recognized as safe" (GRAS), many food-safe substances are not GRAS and their use in some food-related applications may require further regulatory approval in some countries.

B. Water Softener Systems

[0011] Figure 1 schematically illustrates a water softening system in accordance with one embodiment of the invention. The water softening system 10 generally includes an ion exchange tank 20, a regenerating solution reservoir 30, and an antimicrobial agent reservoir 40. A controller 50 may be operatively coupled to one or more valves 52 (identified as valves 52a, 52b, and 52c in Figure 1) to control operation of the water softening system 10.

[0012] The ion exchange tank 20 includes an ion exchange medium 22 through which water passes for treatment. Any suitable ion exchange medium 22 known in the art may be employed, including ion exchange resins and suitable mineral-based media such as zeolites. In normal operation, incoming water, e.g., water from a municipal water supply, is directed by valve 52b into the ion exchange tank 20. Treated or "softened" water exiting the ion exchange tank 20 may pass through valve 52a to deliver soft water for use, e.g., as potable water for a household.

[0013] From time to time, the ion exchange medium 22 may need to be regenerated by exchanging built-up ions removed from the incoming water supply with alternate ions, such as sodium or potassium ions. The controller 50 may be programmed to initiate a regenerating cycle at fixed intervals or on any other suitable basis; a variety of programmable controllers 50 for use in water softening systems 10 are commercially available. At the beginning of a regenerating cycle, the valve 52b may be changed to incoming water into a bypass line 54 for delivery to the first valve 52a. During the regenerating cycle, the valve 52a may direct this bypass water into the conduit conventionally used to deliver the softened water. In this configuration, the second valve 52b may also direct fluid from the regenerating solution tank 30 into the ion exchange tank 20. (Each of the valves 52 may comprise a single valve or a set of valves.) The solution passing through the ion exchange tank 20 may then be diverted by the first valve 52a to waste, e.g., to be discharged to the environment.

[0014] The regenerating solution reservoir 30 may include a ready supply of a regenerating solution 34, which may comprise a dissolved fraction of a salt-based formulation in accordance with other embodiments of the invention or a conventional water-softening salt. The salt formulation may be provided in the form of pellets 32 or in other suitable particulate form, such as pieces that are broken from a large, thick sheet of the salt. The solution 34 typically is about 10 weight percent of the salt.

[0015] The water softening system 10 of Figure 1 also includes an antibacterial agent reservoir 40 that includes an antimicrobial solution 44. The antimicrobial solution 44 may comprise water in which a portion of the pellets 42 or a block of a water-soluble antimicrobial formulation in accordance with select embodiments is dissolved. A quantity of the antimicrobial solution 44 may be delivered to the ion exchange tank 20 during regeneration. In the schematic illustration of Figure 1, the controller 50 would open the valve 52c to deliver the antimicrobial solution 44 to the regenerating solution tank 30. This antimicrobial solution 44 can mix with the regenerating solution 34 for delivery to the ion exchange tank 20. Alternatively, the antimicrobial solution 44 may bypass the regenerating solution reservoir 30, e.g., by being delivered to the second control valve 52b. Alternatively, the regenerating solution 34 and the antimicrobial solution 44 may be delivered to and pass through the ion exchange tank 20 sequentially rather than together. For example, the antimicrobial solution 44 may be delivered to the tank 20, followed either immediately or at a later time by the regenerating solution 34.

[0016] After the regenerating solution 34 and/or antimicrobial solution 44 has passed through the ion exchange medium 22, the valves 52a-c may be returned to their first configuration and operation can return to normal, i.e., with incoming water passing through the ion exchange tank 20 to deliver softened water for use. C. Antimicrobial Formulations and Solutions

[0017] Substantial concentrations of salt make antimicrobial salt formulations and solutions in embodiments of the invention well-suited for a variety of applications, including use in regenerating ion exchange media such as those employed in water softener systems. For ease of understanding, the following discussion refers to the water softener system 10 shown in Figure 1. Antimicrobial formulations and solutions in accordance with aspects of the invention may be used in the water softener system 10, but are also well-suited for use in conventional water softening systems and in other ion exchange-based treatment systems. Further, although the following discussion focuses on use of antimicrobial salt formulations and solutions for such regeneration, they are useful for other purposes, as well, such as in chilled brine processing of meat and other food-safety applications.

[0018] One useful formulation contains about 25-25,000 ppm surfactant, about 0.1-25 weight percent (wt. %.) acid, and about 72.5-99.9 wt. % salt. This formulation can be dissolved in water in the regenerating solution reservoir 30 to make a regenerating solution ranging in concentration from about 1 % total solids by weight (i.e., about 1 wt. % of the salt-based formulation) up to the saturation point. Typically, brine solutions used in regenerating ion exchange media have a salt concentration of about 10 wt. %; regenerating solutions having about 8-11 wt. % of an antimicrobial salt formulation of the invention are expected to work well for the same purpose.

[0019] Suitable surfactants include sodium lauryl sulfate (SLS), linear alkylbenzene sulfonates, alcohol sulfates, alpha-olefin sulfonates, alcohol ethoxylates, nonylphenyl ethoxylates, alkylpolyglucosides, fatty alkanoamides, fatty amine oxides, sodium dioctylsulfosuccinate, dodecylbenzene sulfonic acid and salts thereof. The sodium salt of sulfonated oleic acid, sodium dodecylbenzene sulfonate, and dodecyldiphenyloxide disulfonic acid and salts thereof may also be employed as the surfactant. In one embodiment, the surfactant is soluble in a concentrated aqueous salt solution, e.g., an aqueous solution containing 10 wt. % or more of the salt used in the formulation. Salt-based formulations in accordance with aspects of the invention may include about 50 - 25,000 ppm of at least one, possibly two or more, of these surfactants. SLS at a level of about 100 - 1000 ppm, e.g., about 100 - 500 ppm, is deemed particularly useful for ion exchange media regeneration. [0020] Antimicrobial salt formulations in aspects of the invention also include about 0.3 - 25 wt. % of at least one acid selected from the group consisting of citric, malic, acetic, propionic, lactic, benzoic, ascorbic, isoascorbic, sorbic, phosphoric, hydrochloric, nitric, malic, tartaric, adipic, succinic, glutaric, salicylic, and sulfuric acids and sodium bisulfate. Of these, citric and malic acids are generally preferred, with contents of about 0.4 - 6 wt. %, e.g., about 0.5 - 2 wt. %, being expected to work well for a variety of applications.

[0021] The balance, e.g., about 75 - 99.7 wt. %, of the antimicrobial salt formulations may comprise at least one inorganic salt selected from the group consisting of sodium, potassium, magnesium, calcium, iron, and ammonium salts of chloride, sulfate, nitrate, phosphate, carbonate, and hydroxide. Salts of monovalent cations may be more desirable than polyvalent cation salts, with calcium and potassium salts, e.g., NaCI and KCI, being generally preferred. For anion exchange applications, salts of monovalent anions, e.g., a chloride or nitrate salt, are desirable.

[0022] In some embodiments, though, the balance of the antimicrobial salt formulation may include at least one component other than the salt. For example, the formulation may include a scenting agent to improve the odor of the regenerating solution 34 in the regeneration solution reservoir 30.

[0023] As explained below in connection with the data in Tables 1 to 11 , testing suggests that at least certain surfactant/salt combinations can function as a much more effective antimicrobial agent than either the salt or the surfactant alone.

[0024] Formulations in accordance with the invention may be provided in a variety of forms. In one embodiment, the formulations are blended to yield a relatively homogeneous mixture and this mixture is compressed into pellets of a suitable size. Procedures and apparatus for pelletizing water softener salt are well known in the art and need not be detailed here. The formulations may instead be compressed into larger blocks for more convenient storage and handling. As is also known in the art, the formulation may be formed as a large, thick sheet and broken into suitably sized chunks. If so desired, the ingredients of the formulation may be mixed dry and compressed to form the sheet or the sheet can be formed by mixing the ingredients with a solvent and drying. [0025] As noted above, one embodiment of the invention provides a water softener system 10 that includes a regenerating solution reservoir 30 and an antimicrobial agent reservoir 40. In one embodiment, the pellets 32 in the regenerating solution reservoir 30 may comprise a formulation in accordance with embodiments of the invention and the antimicrobial agent solution 44 can be used in the regenerating cycle on only intermittently or on an as-needed basis. In another embodiment, the pellets 32 may comprise a conventional water softening salt. In either embodiment, the pellets 42 of the antimicrobial agent may include at least one of the acids and/or at least one of the surfactants enumerated above, but at higher levels than in the preceding embodiments. The level of acid and surfactant in the pellets 42 may be selected so that the combination of the regenerating solution 34 and the antimicrobial agent solution 44 in desired proportions will yield a concentration of salt, acid and surfactant analogous to solutions made with the formulations outlined above.

[0026] In one particular embodiment, the antimicrobial formulation 42 in the antimicrobial agent reservoir 40 comprises about 20-35 wt. % of a food-grade acid, e.g., citric or malic acid, and about 0.1-1 wt.% of a food-grade surfactant; one exemplary formulation includes about 25-30 wt. %, e.g., about 28 wt. %, citric acid, and about 0.4 wt. % SLS. The balance of the antimicrobial formulation 42 may comprise an inorganic salt. If deemed necessary, the antimicrobial formulation 42 may also include an encapsulating agent or other additive that can slow dissolving of the formulation to a desirable rate. In an alternative approach useful for conventional water softening systems that do not employ a separate antimicrobial agent reservoir 40, a block or pellets 42 of such a more concentrated antimicrobial formulation 42 may be added directly to the regenerating solution reservoir 30 with conventional salt pellets 32, e.g., commercially available water softener salt. In one illustrative embodiment, a one-pound block of the antimicrobial formulation may be added to the regenerating solution reservoir 30 each time the supply of salt pellets 32 is replenished.

[0027] In another embodiment, the antimicrobial solution 44 may include an acid and a surfactant, but have little or no added salt. An acid/surfactant formulation in this embodiment may be formed into pellets 42 or a block and held in the antimicrobial agent reservoir to make an aqueous solution with added water. Alternatively, the formulation may be in liquid form instead of a solid pellet 42 or the like. This liquid may comprise a concentrate that is mixed with added water in the reservoir 40 or may be delivered in the final desired concentration for addition to the regenerating solution reservoir 30 or directly to the ion exchange tank 20, as described above. One exemplary composition contains about 5 wt. % of an acid, e.g., citric or malic acid, and about 700 ppm of a surfactant, e.g., SLS, and about one eighth of a gallon may be added to the ion exchange medium 22 (either directly or with the regenerating solution 34) in a regenerating cycle for the medium 22.

[0028] Early screening tests indicated that there was an unexpected synergistic effect between sodium chloride and an acid/SLS antibacterial additive. Replicate tests were run to determine if this effect was statistically significant. Ten percent by weight solutions were prepared of a formulation of 0.6 wt. % citric or malic acid, 100 ppm SLS, and 99.4 wt. % sodium chloride. Solutions were also prepared containing an identical concentration of acid and SLS but no sodium chloride. A bacterial culture suspension (Escherichia coli ATCC 11229) that had been incubated for 24 hours in Brain Heart Infusion (BHI) broth and had an initial inoculum count of about 1p⁹ CFU/ml was serially diluted in cold Butterfield's Phosphate Buffered Water (BPBW) to 10⁵ CFU/ml. A 1.0 ml aliquot of this suspension was added to 100 ml of test solution at room temperature and mixed well, providing an initial inoculum of 10³ CFU/ml. After 30 minutes, the E. coli populations were enumerated by plating on tryptic soy agar (TSA), making serial dilutions as necessary in BPBW. Plates were incubated at 35⁰C +/- 2⁰C for approximately 24 hours. Colonies were then counted and compared to the initial inoculum counts. Results of these tests run on 16 replicates of each test solution are given in Table 1.

Table 1. Effectiveness of Acid/SLS Solutions with and without Salt on E. coli

Test Solution Average E. Coli Cone. (CFU/ml) citric acid, SLS, with salt 540 citric acid, SLS, without salt 1054 malic acid, SLS, with salt 141 malic acid, SLS, without salt 2419

[0029] For both the citric acid/SLS and malic acid/SLS additives, the number of bacteria remaining alive after 30 minutes is much lower when salt is present than when there is no salt present. Analysis of the data indicates that there is a statistically significant increase in kill in the presence of salt (p<0.05). In contrast, a 10% solution of pure sodium chloride does not provide any significant kill of the test microorganisms.

[0030] Although the preceding test was carried out in deionized water, the tests reflected in Tables 2 and 3 were carried out in hard water to better simulate actual operation conditions for a water softening application. In general, the anti-bacterial effectiveness of the formulations decreased significantly in hard water, requiring higher acid and/or surfactant contents to achieve the same efficacy. Formulas containing sodium lauryl sulfate and either citric or malic acid, though, were effective in killing both gram negative and gram positive bacteria.

[0031] Replicate tests were next run on formulas containing sodium lauryl sulfate and either citric or malic acid to estimate the acid and/or surfactant content required to consistently provide at least about 65%, desirably at least about 90%, kill rates of the more resistant gram negative bacteria, £. coli. Salt formulations including at least about 100 ppm SLS were deemed more effective than formulations containing lower SLS levels. SLS will cause a small amount of foam formation in saturated brine. Other commercially available surfactants (such as Triton QS44 sold by The Dow Chemical Company of Midland, Michigan, USA) could be substituted for sodium lauryl sulfate to avoid foaming, but many of those surfactants may not be food-safe (as is SLS) and may raise environmental concerns. A summary of the performance of formulations containing 100 ppm sodium lauryl sulfate and various amounts of citric acid or malic acid is given in Table 2, in which runs C1-C10 employed the stated citric acid content in the salt-based formulation and runs M1-M5 used malic acid instead of citric acid. (Again, the SLS and acid concentrations are in the salt- based formulation, not in the resultant solution formed with the formulation.)

Table 2. Percent Kill of E. coli After 30 Minutes in Hard Water*

*The number of replicates in a given experiment is listed parenthetically.

[0032] S. aureus was grown in a fashion directly analogous to that set forth above for growth of the E. coli culture, except that the S. aureus plates were incubated for about 48 hours instead of 24 hours. Results of tests on S. aureus are given in Table 3, in which runs C1-C3 employed the stated citric acid content in the salt-based formulation and runs M1 and M2 used malic acid instead of citric acid. (The tested formulations were generally more effective toward S. aureus than E. coli, so fewer replicates were carried out on S. aureus.)

Table 3. Percent Kill of S. aureus After 30 Minutes in Hard Water*

*The number of replicates in a given experiment is listed parenthetically.

[0033] Based upon the results in Tables 2 and 3, a salt formulation including about 100 ppm sodium lauryl sulfate, about 0.6 wt. % citric acid or malic acid, and about 99.4 wt. % salt significantly decreases (e.g., at least a 65% reduction) both gram negative and gram positive bacteria populations. Increasing the acid content slightly to about 0.7 wt. % consistently killed at least about 90% of both gram negative and gram positive bacteria. As a matter of fact, the 0.7% acid formulas consistently killed about 95% or more of the tested gram negative bacteria and regularly killed at least about 99% of such bacteria.

[0034] The following examples further illustrate the synergistic and unexpected results from combining acid/surfactant with salt. An experiment was run to determine if solutions containing sodium chloride, sodium lauryl sulfate, and various acids would kill L. monocytogenes at cold temperatures. The following test procedure was used: A bacterial culture suspension (L. monocytogenes H2446 [CDC Global Standard]; Scott A-serotype 4b; 12243-serotype 1/2a; and a recent cooked meat and poultry facility isolate, WP4) that had been incubated for at least 5 days in BHl broth and had an initial inoculum count of about 10⁹ CFU/ml was serially diluted in cold BPBW to 10⁵ CFU/ml. A 1.0 ml aliquot of this suspension was added to 100 ml of cold (-7⁰C + 2⁰C) test solution and mixed well, providing an initial inoculum of 10³ CFU/ml. The test solutions were incubated at -7⁰C +/2⁰C for the duration of the experiment. At intervals of 0, 4, and 24 hours the L. monocytogenes populations in the test solutions were determined on Modified Oxford agar (MOX). MOX plates were incubated at 35⁰C +/- 2°C for approximately 48 hours. Colonies were then counted and compared to the initial inoculum counts.

[0035] Results are given in Table 4. Each test solution was a 17% by weight solution of the listed formula prepared in soft water.

[0036] In another experiment, two sets of solutions were tested. The first set (samples 1-12 in Table 5 below) was prepared in hard tap water and contained about 17.0% by mass of the identified formulation. These samples were inoculated with 10³ CFU/ml L. monocytogenes by the same procedure described above. A second set of samples was prepared from brine taken from a ready-to-eat meat processing operation. The recirculated brine had been used to chill packaged meat for one week. After a week of use the brine typically contains various types of aerobic psychrotrophic and mesophilic bacteria. This experiment was done in order to determine if the additives would kill the microorganisms naturally occurring in actual process brine from a plant. Since the spent chill brine samples already contained NaCI, citric acid and/or SLS was added to provide an effective concentration of additive. One set of these samples (samples 13 -17) were inoculated with 10³ L. monocytogenes and the other set (samples 18-22) contained only the naturally occurring organisms in the spent chill brine. Results are given in Table 5 below. The data indicate that at lower acid levels, the SLS increases the effectiveness of the mixture, but at higher acid levels, the SLS is not necessary. The results show the formulations are effective in hard water. The results also demonstrate that the formulations effectively kill L. monocytogenes as well as the naturally occurring microorganisms in spent chill brine from an actual meat processing plant.

Table 5. Effects of Antimicrobial Salt Formulas in Hard Water and in Spent Chill

Brine

[0037] A test was run to determine if salts other than sodium chloride would show a synergistic antimicrobial effect with an acid and sodium lauryl sulfate. Solutions containing 0.6409 grams malic acid and 0.0107 grams sodium lauryl sulfate per liter were prepared with and without 107.0 grams of various salts (added on an anhydrous basis). Solutions were inoculated with E. coli described above and the amount of bacterial kill was measured to determine if the added salt caused an increase in the effectiveness of the acid/surfactant active ingredients. Results are shown in Table 6.

Table 6. Effect of Different Salts on the Antimicrobial Action of Malic Acid/SLS

Solution (salt added) % Kill of E. CoIi No salt addition 4.4% Sodium sulfate 87% Magnesium chloride 56% Potassium chloride 18% Sodium chloride 78% Potassium sulfate 34% Calcium chloride 55% Magnesium sulfate 93%

[0038] Tests run on solutions containing only the salt and no other ingredient indicate that sodium sulfate, potassium chloride, and potassium sulfate alone provide no bacterial kill. Magnesium chloride provided 61% kill, calcium chloride provided 26% kill, and magnesium sulfate provided 10% kill. Thus, based on the data developed thus far, sodium sulfate, sodium chloride, and magnesium sulfate appear to significantly increase the effectiveness of the acid/surfactant antimicrobial agent, even though the salts provide little kill on their own.

[0039] The effectiveness of antimicrobial salt formulas was tested against L. monocytogenes in a biofilm. Stainless steel coupons (2 x 5 cm, type 302 stainless steel, 2B finish) were cleaned in acetone followed by an alkaline detergent and distilled water and then dried in an autoclave at 121⁰C for 15 minutes. A culture of L monocytogenes (Scott A - serotype 4b) was prepared by inoculating 10 mL of TSA and incubating overnight at 35°C. 50 mL of sterile TSA + 0.6% yeast extract (YE) was aseptically dispensed into sterile disposable conical shaped plastic tubes and one drop of overnight grown L. mono culture was added to each tube. Inoculated tubes were incubated at 25°C for approximately 48 hours. After the biofilm had formed on the coupons, a coupon was aseptically removed from the tube and gently rinsed with distilled water to remove unattached cells. Coupons were then immersed in cold antimicrobial test solution (-6.7⁰C) and incubated over different time intervals (1 hour, 24 hours, and 5 days). After incubation period, the coupon was shaken in a tube containing 40 mL of sterile PBW and 10 sterile glass beads (4 mm) for 2 minutes two remove the cells attached to the coupon biofilm. The cells were plated in the PBW on TSA + 0.6% YE using appropriate dilutions and incubated at 35°C for 48 hours.

[0040] Results on triplicate samples of antimicrobial test solutions are given in Table 7 below. Each solution contained 17% by weight of a formula consisting of the percentages of citric acid and SLS listed in Table 7 with the balance of the formula being NaCI in each case. The data indicate that not only are the antimicrobial salt solutions effective at killing bacteria suspended in solution, they are also effective at killing bacteria within a biofilm.

Table 7. Log Concentration of L mono in Antimicrobial Salt Solutions

[0041] Another set of experiments was done in order to determine the effectiveness of different acids and different types of surfactants in the antimicrobial salt formulations. In one experiment, test solutions containing 17% by weight of formulas containing various levels of sodium chloride, 100 ppm sodium lauryl sulfate, and various levels of different acids were tested for effectiveness in killing L monocytogenes at cold temperatures. The same test procedure was used as described above; test solutions were plated on MOX TAL (Modified Oxford medium with a Thin Agar Layer) with TSA. Results are given in Table 8. Table 8. Effect of Different Acids on the Antimicrobial Action of NaCI/Acid/SLS

Sample Time 0 4 Hours

(CFU/ml) (CFU/ml)

Salt control 850 1380

Salt + 100 ppm SLS, 0.5% citric acid 980 890 100 ppm SLS, 99.5% NaCI, 0.9% succinic acid 1230 18 100 ppm SLS, 99.1% NaCI 1070 69 1.5% isoascorbic acid, 100 ppm SLS, 98.5% NaCI 1140 59 1.8% adipic acid, 100 ppm SLS, 98.2% NaCI 900 4 1.6% sorbic acid, 100 ppm SLS, 98.4% NaCI 820 500 1.3% acetic acid, 100 ppm SLS, 98.7% NaCI 1070 230 2.1 % propionic acid, 100 ppm SLS, 97.9% NaCI 1440 6 0.6% lactic acid, 100 ppm SLS, 99.4% NaCI 1050 220 1.6% ascorbic acid, 100 ppm SLS, 98.4% NaCI 1230 54 0.3% formic acid, 100 ppm SLS, 99.7% NaCI 1930 38 0.3% phosphoric acid, 100 ppm SLS, 99.7% NaCI 1050 17 0.1 % hydrochloric acid, 100 ppm SLS, 99.9% NaCI 1100 44 0.3% tartaric acid, 100 ppm SLS, 99.7% NaCI 1180 410 1.1 % glutaric acid, 100 ppm SLS, 98.9% NaCI 610 180 1.2% benzoic acid, 100 ppm SLS, 98.8% NaCI 1020 17 0.5% salicylic acid, 100 ppm SLS, 99.5% NaCI 1100 5 0.2% sulfuric acid, 100 ppm SLS, 99.8% NaCI 830 0

[0042] In another experiment, test solutions containing 17% by weight of formulas containing 99.7% sodium chloride, 0.3% citric acid, and 500 ppm of various types of surfactants were tested for effectiveness in killing L monocytogenes at cold temperatures. The same test procedure was used as described above; test solutions were plated on MOX TAL (Modified Oxford Medium with a Thin Agar Layer) with TSA. Results are given in Table 9.

Table 9. Effect of Different Acids on the Antimicrobial Action of NaCI Surfactant

Tested

Surfactant Tested Time 0 4 Hours

(CFU/ml) (CFU/ml)

Salt Control (no additive) 880 610 polyoxyethylene-polyoxypropylene block polymer 820 610 sodium salt of sulfonated oleic acid 240 0 sodium xylene sulfonate 910 820 dodecyl diphenyl oxide disulfonate 0 0 Surfactant Tested Time O 4 Hours

(CFU/ml) (CFU/ml) sodium linear alkyl-benzene sulfonate 490 0 alpha-olefin sulfonate 370 0

Alkylpolyglucoside 280 0 nonylphenol ethoxylate 460 0 fatty alkanolamide 470 0 alcohol ethoxylate 1080 1 lauramine oxide 2 0

[0043] Thus, the data indicate that solutions of salt, acid, and surfactant provide efficient kill of bacteria even at temperatures below the freezing point of water. Salts such as sodium sulfate, sodium chloride, and magnesium sulfate act synergistically with the acid and surfactant to enhance the antimicrobial effectiveness. The formulations are shown to be effective in killing pathogenic bacteria such as L. monocytogenes. The formulas were shown to be effective both in freshly prepared brines and in spent process chill brine from a ready-to-eat meat plant. The levels of acid and surfactant may be varied to suit the particular application; reducing the concentration of the acid may be compensated by raising the concentration of surfactant and vice versa. In addition to effectively killing bacteria suspended in solutions, the formulas are also shown to be effective at killing bacteria within a biofilm.

[0044] Further tests were conducted to determine the antimicrobial efficacy of a salt formulation containing a surfactant but no added acid. The effect of an aqueous solution comprising about 20 wt.% of various salt and salt/surfactant formulations on L monocytogenes were tested in a manner directly analogous to that set forth above in connection with the data in Table 4. Table 10 sets forth the compositions and the L. monocytogenes population (stated as the log of the concentration of the bacteria) found after 4 hours of incubation. [Note that the compositions in Table 10 and in Table 11 , below, state the concentration in the solution, not in the salt concentrate. Since the solutions are 20 wt. % of the salt formulation, the concentration of surfactant in the salt formulation would be about five times the stated concentration in the solution.] Table 10. Effect of Solutions of NaCI and SLS on L. monocytogenes

* The 3.90 value is an average of two runs that yielded values of 3.84 and 3.95. **The 0.85 value is an average of two runs that yielded values of 0.70 and 1.00

[0045] Further tests were run on a variety of different surfactants, demonstrating that a variety of different types of surfactants show a strong synergistic effect in combination with sodium chloride:

Table 11. Effect of Solutions of NaCI and various surfactants on L monocytogenes

[0046] Hence, formulations in other embodiments of the invention may comprise ah inorganic salt and at least about 200 ppm of a surfactant, e.g., about 250-5000 ppm, e.g., 500-1500 ppm, of the surfactant. Such formulations are deemed particularly useful in food safety applications.

[0047] The foregoing specification describes this invention in relation to certain preferred embodiments, and many details have been set forth for purpose of illustration. As those skilled in the art will appreciate, however, the invention is susceptible to additional embodiments and that some of the details mentioned above can be varied considerably without departing from the basic principles of the invention.

Claims

CLAIMSWe claim:

1. An antimicrobial water softening composition for use in regenerating an ion exchange medium, comprising: about 100 - 25,000 ppm of at least one surfactant selected from the group consisting of sodium lauryl sulfate, linear alkylbenzene sulfonates, alcohol sulfates, alpha-olefin sulfonates, alcohol ethoxylates, nonylphenyl ethoxylates, alkylpolyglucosides, fatty alkanoamides, fatty amine oxides, sodium dioctylsulfosuccinate, dodecylbenzene sulfonic acid and salts thereof; the sodium salt of sulfonated oleic acid, sodium dodecylbenzene sulfonate, dodecyldiphenyloxide disulfonic acid and salts thereof; about 0.3 - 25 weight percent (wt. %) of at least one acid selected from the group consisting of citric, malic, acetic, propionic, lactic, benzoic, ascorbic, isoascorbic, sorbic, phosphoric, hydrochloric, nitric, malic, tartaric, adipic, succinic, glutaric, salicylic, and sulfuric acids and sodium bisulfate; and about 75 - 99.7 wt. % of at least one inorganic salt selected from the group consisting of sodium, potassium, magnesium, calcium, iron, and ammonium salts of chloride, sulfate, nitrate, phosphate, carbonate, and hydroxide.

2. The composition of claim 1 wherein the acid comprises at least about 0.1 wt. % phosphoric acid and at least about 0.3 wt. % of an acid selected from the group consisting of citric and malic acids.

3. The composition of claim 1 wherein the surfactant comprises at least about 100 ppm of sodium lauryl sulfate.

4. The composition of claim 1 further comprising a food-grade scent compounds.

5. An antimicrobial water softening composition for use in regenerating an ion exchange medium, comprising: about 0.3 - 6 wt. % citric acid, malic acid, or a combination of citric acid and malic acid; about 100 - 500 ppm sodium lauryl sulfate; and about 94 - 99.7 wt. % sodium chloride, potassium chloride, or a combination of sodium chloride and potassium chloride.

6. The antimicrobial water softening composition of claim 5 wherein the salt comprises salt pellets.

7. A method of regenerating an ion exchange medium having a bacterial population, comprising dissolving a salt formulation in water to create a brine and passing the brine through the ion exchange medium during a regenerating cycle, wherein the salt formulation comprises a food-grade acid, at least about 100 ppm of a food-grade surfactant, and at least about 90 wt. % of an inorganic, water-soluble salt of sodium, potassium, or sodium and potassium and wherein the acid and the surfactant are present in the brine in an amount efficacious to kill at least about 65% of gram negative bacteria in the bacterial population as a result of the regenerating cycle.

8. The method of claim 7 wherein the acid and the surfactant are present in the brine in an amount efficacious to kill at least about 80% of gram negative bacteria in the bacterial population as a result of the regenerating cycle.

9. The method of claim 7 wherein the acid and the surfactant are present in the brine in an amount efficacious to kill at least about 90% of gram negative bacteria in the bacterial population as a result of the regenerating cycle.

10. The method of claim 7 wherein the acid and the surfactant are present in the brine in an amount efficacious to also kill at least about 70% of gram positive bacteria in the bacterial population as a result of the regenerating cycle.

11. The method of claim 7 wherein the acid and the surfactant are present in the brine in an amount efficacious to kill at least about 80% of gram negative bacteria and at least about 80% of gram positive bacteria in the bacterial population as a result of the regenerating cycle.

12. The method of claim 7 wherein the acid comprises citric acid, malic acid, or citric and malic acids.

13. The method of claim 7 wherein the salt formulation includes about 0.6-6 wt. % of the acid.

14. The method of claim 7 wherein the salt formulation includes about 0.6-6 wt. % of the acid and the acid comprises citric acid, malic acid, or citric and malic acids.

15. The method of claim 7 wherein the surfactant comprises sodium lauryl sulfate.

16. The method of claim 7 wherein the salt formulation includes a scent agent in an amount sufficient to give the brine a noticeable odor.

17. A water softening system comprising: an ion exchange tank; a regeneration solution reservoir comprising regeneration solution; and an antimicrobial agent reservoir comprising an antimicrobial solution; a controller, wherein the controller may be programmed to initiate a regeneration cycle such that the regeneration solution and antimicrobial solution are delivered to the ion exchange tank.

18. The system of claim 17 wherein the regeneration solution and antimicrobial solution are mixed prior to delivery to the ion exchange tank. 9. The system of claim 17 wherein the regeneration solution and antimicrobial solution delivered to the ion exchange tank sequentially.