WO2006068892A1 - Stretchable absorbent core and wrap - Google Patents
Stretchable absorbent core and wrap Download PDFInfo
- Publication number
- WO2006068892A1 WO2006068892A1 PCT/US2005/045159 US2005045159W WO2006068892A1 WO 2006068892 A1 WO2006068892 A1 WO 2006068892A1 US 2005045159 W US2005045159 W US 2005045159W WO 2006068892 A1 WO2006068892 A1 WO 2006068892A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- stretchable
- absorbent
- core wrap
- absorbent article
- core
- Prior art date
Abstract
Description
Claims