WO2006081156A2 - Non-combustible reinforced cementitious lightweight panels and metal frame system for a fire wall and other fire resistive assemblies - Google Patents
Non-combustible reinforced cementitious lightweight panels and metal frame system for a fire wall and other fire resistive assemblies Download PDFInfo
- Publication number
- WO2006081156A2 WO2006081156A2 PCT/US2006/002196 US2006002196W WO2006081156A2 WO 2006081156 A2 WO2006081156 A2 WO 2006081156A2 US 2006002196 W US2006002196 W US 2006002196W WO 2006081156 A2 WO2006081156 A2 WO 2006081156A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- panel
- fire
- wall
- panels
- scp
- Prior art date
Abstract
Description
Claims