WO2006124831A1 - Process for making non-continuous articles with microstructures - Google Patents
Process for making non-continuous articles with microstructures Download PDFInfo
- Publication number
- WO2006124831A1 WO2006124831A1 PCT/US2006/018822 US2006018822W WO2006124831A1 WO 2006124831 A1 WO2006124831 A1 WO 2006124831A1 US 2006018822 W US2006018822 W US 2006018822W WO 2006124831 A1 WO2006124831 A1 WO 2006124831A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- coating device
- coating
- roll
- casting roll
- Prior art date
Abstract
Description
Claims