WO2007021633A2 - Process for sulfur adsorption using copper-containing catalyst - Google Patents
Process for sulfur adsorption using copper-containing catalyst Download PDFInfo
- Publication number
- WO2007021633A2 WO2007021633A2 PCT/US2006/030693 US2006030693W WO2007021633A2 WO 2007021633 A2 WO2007021633 A2 WO 2007021633A2 US 2006030693 W US2006030693 W US 2006030693W WO 2007021633 A2 WO2007021633 A2 WO 2007021633A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- sulfur
- copper
- lhsv
- per hour
- Prior art date
Abstract
The present invention is a method for the adsorption of sulfur-containing compounds from a hydrocarbon feedstream, and in particular, an olefin feedstream. The method comprises contacting the sulfur-containing compound with a copper oxide / zinc oxide / aluminum oxide catalyst optionally promoted with a metal.
Description
Title: Process for Sulfur Adsorption Using Copper-Containing Catalyst
Inventors: Turbeville et al Attorney Docket: 20060515-004
Background of Invention
This invention is directed to catalysts and related processes useful for sulfur adsorption from sulfur compound containing feedstreams. Specifically, the invention is directed to copper oxide / zinc oxide / aluminum oxide catalyst optionally promoted with an alkali metal, such as K, Rb, Cs, or with a metal selected from the group consisting of Ti, V, Mn, Zr, Mo, Ru, RIi, Pd, Ba, La, Re, Tl, Ce and combinations thereof, useful for sulfur adsorption processes.
As used herein, the term adsorption shall be defined broadly so as to also include absorption, and no attempt shall be made to distinguish adsorption or adsorptive processes from absorption or absorptive processes.
As part of the pretreatment of naphtha feed streams for catalytic reformers and isomerization units, sulfur guards are commonly used to polish the remaining sulfur species that are present after a hydtrotreater. Guard materials often contain either reduced nickel or copper oxide. Nickel adsorbents are very effective at adsorbing most if not all of the sulfur compounds from the feed stream. Copper containing adsorbents are also effective at taking out sulfur, especially H2S, but are known to allow other sulfur compounds to partially or completely pass through the guard bed, including sulfides and thiophenes. Depending on the catalyst and application, the fact that some sulfur passes through a guard bed may be acceptable since sulfur is often used to moderate the downstream catalyst performance to the desired level. Ia general, however, thiophenes are less desirable as the sulfur form than, for example, disulfides.
In addition to adsorbents, a number of different catalysts are known in the art that are effective for removing sulfur compounds. For example, activated carbon has a high capacity for ethyl mercaptans, manganese oxide is effective for dimethyl sulfoxide removal, and zinc oxide can be used to remove hydrogen sulfide. Other catalysts known to be effective in desulfurization processes include carbon, copper / zinc oxides, nickel-based sorbents, nickel oxides, zeolites, molecular sieves and faujasites, among others. In addition, different methods have been used to reduce the sulfur level in feedstreams,
Page l
Title: Process for Sulfur Adsorption Using Copper-Containing Catalyst
Inventors: Turbeville et al Attorney Docket: 20060515-004 such as prior art hydrodesulfurization (HDS) processes. These processes are usually carried out at high temperatures and pressures, so they are relatively expensive processes. Further, the HDS processes normally only reduce the sulfur content in gasoline feedstreams to levels of about 200 ppm whereas it is desirable to reduce the sulfur content to about 10 ppm. Thus, a better method for removal of unacceptable sulfur-containing compounds is needed.
Summary of the Invention
The present invention is a method for the adsorption of sulfur-containing compounds from a hydrocarbon feedstream. The method comprises contacting the sulfur-containing compound with a copper oxide / zinc oxide / aluminum oxide catalyst optionally promoted with an alkali metal, such as K, Rb, Cs, or with a metal selected from the group consisting of Ti, V, Mn, Zr, Mo, Ru, RIi, Pd, Ba, La, Re, Tl, Ce and combinations thereof, wherein the catalyst is prepared from a hydroxycarbonate precursor having from about 1% to about 60% of the catalyst aluminum intercalated in a hydrotalcite, wherein the hydrotalcite is defined as (Cu1Zn^Al2 (OH)i6Cθ3-4H2O, and wherein the promoter is applied so as to be accessible at the surface layer of the catalyst.
Detailed Description of the Invention
The present development is a process for improved sulfur adsorption using a copper oxide catalyst. The catalyst comprises copper oxide, zinc oxide and alumina, and optionally a promoter selected from the group consisting of Ti, V, Mn, Zr, Mo, Ru, Rh, Pd, Ba, La, Re, Tl, Ce, and an alkali metal, such as K, Rb, Cs, and combinations thereof. The catalyst is produced from a mixed metal hydroxycarbonate precursor having less than about 60% of the aluminum intercalated in hydrotalcite. The resulting catalyst has been surprisingly discovered to be a more effective sulfur adsorbent material than otherwise similar compositions disclosed in the prior art. The catalyst is similar in composition,
Title: Process for Sulfur Adsorption Using Copper-Containing Catalyst
Inventors: Turbeville et al Attorney Docket: 20060515-004 physical properties and method of preparation as the water gas shift catalyst taught and claimed in U.S. Patents 6,627,572 and 6,693,057, which are incorporated herein in their entirety by reference.
Copper oxide / aluminum oxide catalysts and copper oxide / zinc oxide / alumina catalysts made by methods other than taught in the '572 and '057 patents are known in the art for sulfur adsorption. It has been surprisingly discovered herein that the copper oxide / zinc oxide / alumina catalysts made by the method taught in the '572 and '057 patents demonstrate sulfur adsorption at least two times greater than the prior art sulfur adsorbents.
The catalysts that perform as anticipated can be prepared with up to about 90% of the aluminum intercalated in hydrotalcite. In an exemplary embodiment, without limitation, from about 1% to about 60% of the aluminum is intercalated in hydrotalcite, and preferably from about 5% to about 45% of the aluminum is intercalated in hydrotalcite. For this invention, the term "hydrotalcite" is limited to ternary mixtures of copper, zinc and aluminum with the general structure of (Cu3Zn)6Al2 (OH)i6CO3*4H2O. For this invention, the term "hydrotalcite aluminum" or "HTAl" refers to the concentration of aluminum that is present in the precursor in the form of hydrotalcite divided by the total aluminum concentration of the catalyst. To prepare the desulfurization catalyst, appropriate quantities of copper salts and zinc salts are mixed with an aluminum component in an aqueous solution to produce a catalyst precursor mixture, as taught in the '572 and '057 patents.
The catalyst may be formed into any conventional product shape, such as a tablet. Preferred methods for the preparation of the catalyst shape include pelletizing or other conventional molding processes to produce catalysts, especially in the form of spheres, pellets, rings, tablets or extruded products formed mostly of solid or hollow objects in order to achieve high geometric surface with simultaneously low resistance to flow.
The chemical composition of the catalyst before reductive activation, expressed by weight percentage based on dry weight (no volatile content) after calcination is from about 5% to 70% copper oxide, from about 20% to 50% zinc oxide, and from about 5% to about 50% aluminum oxides.
Title: Process for Sulfur Adsorption Using Copper-Containing Catalyst
Inventors: Turbeville et al Attorney Docket: 20060515-004
Alternatively, more preferred ranges for the materials are: the copper oxide may be present at from about 30% to about 60%, the zinc oxide at from about 20% to about 50%, and the aluminum oxide at from about 5% to about 20%.
The catalyst produced by the process as taught in the '572 and '057 patents has a surface area of from about 40 m2/g to about 200 m2/g, a copper surface area of greater than about 15 m2/g, and a pore volume of from about 0.2 cc/g to about 0.4 cc/g. Optionally, the catalyst may further comprise from about 50 ppm to about 20 wt% promoter, wherein said promoter is selected from the group consisting of potassium, cesium, rubiniurn, titanium, zirconium, manganese, vanadium, molybdenum, ruthenium, rhodium, palladium, barium, lanthanum, rhenium, thallium, cerium, a Group I metal, a Group IV-B metal and combinations thereof.
It has been discovered that catalysts prepared according the the '572 and '057 patents demonstrate sulfur-trapping behavior. These catalysts are particularly effective sulfur traps when the catalyst bed is held at a temperature of from about 3000F up to about 375°F, but are also effective at temperatures as low as about 2500F.
The process for sulfur adsorption involves contacting a sulfur-containing feedstream with the catalyst at a temperature of from about 2500F up to about 375°F while maintaining a pressure of from about 50 psig to about 250 psig, and preferably at about 150 psig. The feed rate may vary, and in an exemplary run the LHSV (liquid-hourly space velocity) is from about 1 per hour to about 10 per hour, and preferably from about 4 per hour to about 5 per hour.
The following information is presented for example only, and is not intended to be limiting in any way: The catalysts used in examples 1 - 7 are specified in Table I below. The physical properties of each Example catalyst is provided in Table II.
Title: Process for Sulfur Adsorption Using Copper-Containing Catalyst
Inventors: Turbeville et al Attorney Docket: 20060515-004
Table I
Table II
Example Catalysts 1 - 7 are evaluated for sulfur trapping using accelerated performance testing procedures. A dual fixed bed unit with temperatures of about 3000F, pressure of about 150 psig, LHSV of about 5 hr'1 is provided with a feed stream of naptha having about 200 ppm by weight sulfur in the form of butanethiol. Breakthrough is defined as 80% sulfur detected in feed exiting the fixed bed. The hours on stream and breakthrough time for each Example Catalyst is provided in Table III. The total sulfur pickup at breakthrough is calculated based on the total hours on stream.
Title: Process for Sulfur Adsorption Using Copper-Containing Catalyst
Inventors: Turbeville et al Attorney Docket: 20060515-004
Table III
The efficiency of these reactions seems to be dependent on the total and copper specific surface areas of the catalyst used. This is especially true for highly dispersed copper on CuO/ZnO/alumina materials.
The principals, preferred embodiments and modes of operation of the present invention have been described in the foregoing specification. The invention which is intended to be protected herein, however, is not to be construed or limited to the particular terms of disclosure, as these are to be regarded as being illustrative rather than restrictive. Variations and changes may be made by those skilled in the art without departing from the spirit of the invention.
Claims
1. A process for the adsorption of sulfur from a hydrocarbon feedstream comprising contacting the feedstream with a catalyst at a temperature of from about 2500F up to about 3750F and at a pressure of from about 50 psig to about 250 psig and wherein the sulfur-containing feedstream contacts the catalyst at a feed rate defined in terms of LHSV and the LHSV is from about 1 per hour to about 10 per hour, and wherein said catalyst comprises from about 5 wt% to about 70 wt% copper oxide, from about 20 wt% to about 50 wt% zinc oxide, and from about 5 wt% to about 50 wt% aluminum oxide, said catalyst being prepared from a precursor material comprising aluminum, wherein from about 1% to about 60% of said aluminum is intercalated in a hydrotalcite, wherein said hydrotalcite is defined as (Cu,Zn)6Al2(OH)i6Cθ3-4H2θ.
2. The process of Claim 1 wherein the sulfur-containing feedstream contacts the catalyst at a pressure of from about 150 psig.
3. The process of Claim 1 wherein the sulfur-containing feedstream contacts the catalyst at a feed rate defined in terms of LHSV and the LHSV is from about 4 per hour to about 5 per hour.
4. The process of Claim 1 wherein said precursor comprises from about 5% to about 45% of said aluminum is intercalated in hydrotalcite.
5. The process of Claim 1 wherein said catalyst further comprises from about 50 ppm to about 20 wt% promoter, wherein said promoter is selected from the group consisting of potassium, cesium, rubinium, titanium, zirconium, manganese, vanadium, molybdenum, ruthenium, rhodium, palladium, barium, lanthanum, rhenium, thallium, cerium, a Group I metal, a Group IV- B metal and combinations thereof.
Title: Process for Sulfur Adsorption Using Copper-Containing Catalyst
Inventors: Turbeville et al Attorney Docket: 20060515-004
6. The process of Claim 5 wherein said promoter comprises about 50 ppm to about 2.0% of said catalyst.
7. The process of Claim 1 wherein said catalyst further defines a surface area and said surface area is from about 40 m2/g to about 200 m2/g.
8. The process of Claim 1 wherein said catalyst further defines a pore volume and said pore volume is from about 0.2 cc/g to about 0.4 cc/g.
9. The process of Claim 1 wherein said copper surface area is at least about 15 m2/g.
10. A process for the adsorption of sulfur from a hydrocarbon feedstream comprising contacting the feedstream with a catalyst at a temperature of from about 2500F up to about 375°F and wherein said catalyst comprises from about 5 wt% to about 70 wt% copper oxide, from about 20 wt% to about 50 wt% zinc oxide, and from about 5 wt% to about 50 wt% aluminum oxide, and said catalyst further defines a surface area and said surface area is from about 40 m2/g to about 200 m2/g and wherein said catalyst further defines a pore volume and said pore volume is from about 0.2 cc/g to about 0.4 cc/g.
11. The process of Claim 10 wherein the sulfur-containing feedstream contacts the catalyst at a pressure of from about 50 psig to about 250 psig.
12. The process of Claim 11 wherein the sulfur-containing feedstream contacts the catalyst at a pressure of from about 150 psig.
Title: Process for Sulfur Adsorption Using Copper-Containing Catalyst
Inventors: Turbeville et al Attorney Docket: 20060515-004
13. The process of Claim 10 wherein the sulfur-containing feedstream contacts the catalyst at a feed rate defined in terms of LHSV and the LHSV is from about 1 per hour to about 10 per hour.
14. The process of Claim 13 wherein the sulfur-containing feedstream contacts the catalyst at a feed rate defined in terms of LHSV and the LHSV is from about 4 per hour to about 5 per hour.
15. The process of Claim 10 wherein said catalyst further comprises from about 50 ppm to about 20 wt% promoter, wherein said promoter is selected from the group consisting of potassium, cesium, rubinium, titanium, zirconium, manganese, vanadium, molybdenum, ruthenium, rhodium, palladium, barium, lanthanum, rhenium, thallium, cerium, a Group I metal, a Group IV- B metal and combinations thereof.
16. A process for the adsorption of sulfur from a hydrocarbon feedstream comprising contacting the feedstream with a catalyst comprising from about 5 wt% to about 70 wt% copper oxide, from about 20 wt% to about 50 wt% zinc oxide, from about 5 wt% to about 50 wt% aluminum oxide, said catalyst being prepared from a precursor material comprising aluminum, wherein from about 1% to about 60% of said aluminum is intercalated in a hydrotalcite, wherein said hydrotalcite is defined as (Cu,Zn)6Al2(OH)i6Cθ3-4H2θ.
17. The process of Claim 16 wherein said catalyst further comprises from about 50 ppm to about 20 wt% promoter, wherein said promoter is selected from the group consisting of potassium, cesium, rubinium, titanium, zirconium, manganese, vanadium, molybdenum, ruthenium, rhodium, palladium, barium, lanthanum, rhenium, thallium, cerium, a Group I metal, a Group IV- B metal and combinations thereof.
Title: Process for Sulfur Adsorption Using Copper-Containing Catalyst
Inventors: Turbeville et al Attorney Docket: 20060515-004
18. The process of Claim 16 wherein the sulfur-containing feedstream contacts the catalyst at a temperature of from about 250°F up to about 3750F.
19. The process of Claim 16 wherein the sulfur-containing feedstream contacts the catalyst at a pressure of from about 50 psig to about 250 psig.
20. The process of Claim 16 wherein the sulfur-containing feedstream contacts the catalyst at a feed rate defined in terms of LHSV and the LHSV is from about 1 per hour to about 10 per hour.