WO2015092615A1 - Strong polyolefin-based thermoplastic elastomeric films and methods of making - Google Patents
Strong polyolefin-based thermoplastic elastomeric films and methods of making Download PDFInfo
- Publication number
- WO2015092615A1 WO2015092615A1 PCT/IB2014/066729 IB2014066729W WO2015092615A1 WO 2015092615 A1 WO2015092615 A1 WO 2015092615A1 IB 2014066729 W IB2014066729 W IB 2014066729W WO 2015092615 A1 WO2015092615 A1 WO 2015092615A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- styrene
- thermoplastic elastomeric
- weight
- elastomeric film
- set forth
- Prior art date
Abstract
Description
Claims